Abstract:In this study, aluminophosphate molecular sieve AlPO4-11, with one-dimensional elliptical channels, was investigated under high pressure in non-penetrating silicone oil by X-ray powder diffraction, infrared spectroscopy and theoretical simulation, focusing on its intrinsic and template-modified mechanical behaviors. Two distinct compressible regimes were observed for both the calcined and as-synthesized AlPO4-11 frameworks before pressure-induced amorphization (PIA). The channel cross-section in the calcined AlPO4-11 framework showed an obvious increase in the ellipticity during this process. The framework structure began to lose crystallinity at approximately 2–3 GPa and underwent significant amorphization at 6.6 GPa. PIA was mainly induced via the destruction of the constructed species along the periodic crystallographic planes which are parallel to the channel axis. The bulk moduli showed that this empty framework was rather soft in these regimes. For the as-synthesized AlPO4-11 framework, the mechanical stability of the channels was markedly improved by the template molecules. A different elliptic deformation of the cross-section with a reduced contractility in the minor axis direction was presented. Discontinuous volume evolution occurs at 3–4 GPa and significant amorphization was postponed to 13.7 GPa. The as-synthesized AlPO4-11 was stiffer than calcined AlPO4-11 and showed a soft to hard transformation due to the strengthened host-guest interaction upon compression. Moreover, infrared spectra indirectly confirmed the structural collapses by detecting the vibrational characteristics of the embedded template molecules. The present results provided a comparative and basic knowledge of the intrinsic and extrinsic stability, compressibility, channel deformation and collapse of the AlPO4-11 framework under high pressure. This study emphasized the importance of guest molecules in modifying the mechanical behaviors of zeolites and resisting framework collapse.

Insertion of N2 into the Channels of AFI Zeolite under High Pressure

High-pressure Behavior of Bromine Confined in the One-Dimensional Channels of Zeolite AlPO4-5 Single Crystals.

Raman and Synchrotron X‐ray Diffraction Studies of 4‐azidobenzoic Acid under High Pressures

Transformation of Ammonium Azide at High Pressure and Temperature

High-pressure and high-temperature induced polymerization of confined nitrogen

The pressure-induced amorphous state of acetonitrile

High-Pressure Studies of Trimethylsilane Azide by Raman Scattering and Synchrotron X-ray Diffraction

Combined X-ray Diffraction and Raman Study of Molecular and Nonmolecular Phases of Nitrogen at High Pressure

Formation of the -N(no)n(no)- Polymer at High Pressure and Stabilization at Ambient Conditions

Structural Transformation Of Molecular Nitrogen To A Single-Bonded Atomic State At High Pressures

Nitrogen Impacts on Structural Stability of Feldspar: Constraints from High Temperature and High Pressure Spectroscopy and Machine Learning

Ionic Conduction in Sodium Azide under High Pressure: Experimental and Theoretical Approaches

High Pressure Behaviors and Novel High-Pressure Phase of Si3N4 and TiN

High-Pressure Studies of Rubidium Azide by Raman and Infrared Spectroscopies

Investigations on the intrinsic and template-dependent transformations of AlPO4-11 molecular sieve under high pressure

High Pressure Raman Scattering Studies on Ammonia Hemihydrate

Polymerization of Nitrogen in Cesium Azide under Modest Pressure

Pressure-stabilized polymerization of nitrogen in manganese nitrides at ambient and high pressures

Ammonia Adsorption at High Temperature and Pressure using Sodium Containing Aluminosilicates: Selectivity over Nitrogen and Multicycle Working Capacities

Excellent capture of N2O functioning at RT and the lower pressure by utilizing NaCaA-85 zeolite

Preservation of high-pressure volatiles in nanostructured diamond capsules