Intermetallic ZrPd 3 -Embedded Nanoporous ZrC as an Efficient and Stable Catalyst of the Suzuki Cross-Coupling Reaction
Yangfan Lu,Tian-Nan Ye,Sang-Won Park,Jiang Li,Masato Sasase,Hitoshi Abe,Yasuhiro Niwa,Masaaki Kitano,Hideo Hosono
DOI: https://doi.org/10.1021/acscatal.0c03416
IF: 12.9
2020-11-24
ACS Catalysis
Abstract:The Suzuki cross-coupling reaction, which is generally catalyzed by Pd-based materials, is a practical approach to create C–C bonds. Although heterogeneous catalysts, including metal-loaded and intermetallic catalysts, afford simple reaction conditions and catalyst reusability, it is challenging to achieve high catalytic activity, durability, and Pd-atom economy together in a single catalyst. Herein, we report the successful preparation of Pd–ZrC, a Pd-based catalyst with the described desirable features. In it, a-few-nanometer-sized nanoparticles of intermetallic ZrPd3 are uniformly dispersed on the surface of nanoporous ZrC with a surface area of 340–450 m2 g–1. As a result of the presence of electron-rich Pd sites and the material’s strong electron-donating ability, Pd–ZrC achieved high catalytic performance in Suzuki cross-coupling reactions at room temperature. Because a low Pd content (1 wt %) is sufficient to produce highly catalytically active Pd–ZrC, this material represents a great improvement in terms of Pd-atom economy over previously reported catalysts. Moreover, no catalytic degradation was noted over up to the presented 15 reaction cycles as the active Pd sites were stabilized in the ZrPd3 lattice. These results indicate that Pd–ZrC has the advantages of both metal-loaded and intermetallic catalysts, providing an approach to enhance the degree of freedom for designing heterogeneous catalysts.
chemistry, physical