A Wearable, Nozzle-Diffuser Microfluidic Pump Based On High-Performance Ferroelectric Nanocomposites
Fengwan Zhao,Xiaoming Chen,Jie Zhang,Xiaohui Zhang,Jun Xie,Li Jin,Zenghui Liu,Jian Zhuang,Wei Ren,Zuo-Guang Ye
DOI: https://doi.org/10.1016/j.snb.2021.130611
2021-01-01
Abstract:New target applications for microfluidic devices have been focused on home usability, wearability and cost-effectiveness. Towards these goals, in this work, a controllable, bendable, and all-organic, nozzle-diffuser microfluidic pump was designed, fabricated and tested. First, to resolve the crucial issue of high driving voltage, the ferroelectric polymer poly(vinylidene fluoride-trifluoroethylene) (P(VDF-TrFE)) was optimized by adding core-shell structured Al2O3@CNT nanofillers. The membrane so developed with 1.1 wt% Al2O3@CNT showed an increase by nearly 7 times in the induced strain in comparison to the neat P(VDF-TrFE) at low electric fields, because the modified membrane simultaneously achieved a lower coercive electric field and a higher polarization. Accordingly, the required operating voltage of the microfluidic pump integrated with optimized membrane significantly decreased from 1000 V to 160 V. Meanwhile, this pump exhibited a wider range of flow rates (13-135 mu L/min) than the reported results, associated with the higher output pressure in our membranes. Importantly, the designed pump still possessed an excellent controllability of the fluidic processes, though it underwent a large bending up to 74 degrees. Consequently, the extremely promising application of the as-prepared microfluidic pump in wearable, biomedical devices was demonstrated.