Abstract:Macroscopic fibers of carbon nanotubes (CNT) have emerged as an ideal architecture to exploit the exceptional properties of CNT building blocks in applications ranging from energy storage to reinforcement in structural composites. Controlled synthesis and scalability are amongst the most pressing challenges to further materialize the potential of CNT fibers. This workshows that under floating catalyst chemical vapor conditions in the direct spinning method, used both in research and industry,the ceramic reactor tube plays an unsuspected active role in CNT growth, leading for example to doubling of reaction yield when mullite (Al4+2xSi2-2xO10-x(x = 0.4)) is used instead of alumina (Al2O3), but without affecting CNT morphology in terms of number of layers, purity or degree of graphitization. This behaviour has been confirmed for different carbon sources andwhen growing either predominantly single-walled or multi-walled CNTs by adjusting promotor concentration. Analysis of large Si-based impurities occasionally found in CNT fiber fabric samples, attributed to reactor tube fragments that end up trapped inthe porous fibers, indicate that the role of the reactor tube is in catalyzing the thermal decomposition of hydrocarbons, which subsequently react with floating Fe catalyst nanoparticles and produce extrusion of the CNTs and formation of an aerogel. Reactor gas analysis confirms that extensive thermal decomposition of the carbon source occurs in the absence of Fe catalystparticles, and that the concentration of different carbon species (e.g. carbon dioxide and ethylene) is sensitive to the reactor tube type. These finding open new avenues for controlled synthesis of CNT fibers by decoupling precursor decomposition from CNT extrusion at the catalyst particle.

Carbon Nanotube Fibers Spun from a Sizing Material

Expanded Carbon Nanotube Fiber at the Liquid-Air Interface for High-Performance Fiber-Based Supercapacitors and Electrochemical Sensors

Carbon nanotube/poly(vinyl alcohol) fibers with a sheath-core structure prepared by wet spinning

Liquid-Crystal Phase Reinforced Carbon Nanotube Fibers

Fabrication of Microscale Carbon Nanotube Fibers

Single Carbon Fibers with a Macroscopic-Thickness, 3D Highly Porous Carbon Nanotube Coating

Wet-spinning of carbon nanotube fibers: dispersion, processing and properties

Fabrication of Carbon Nanotubes/carbon Fiber Hybrid Fiber in Industrial Scale by Sizing Process

Continuous and Scalable Fabrication and Multifunctional Properties of Carbon Nanotube Aerogels from the Floating Catalyst Method

Physical Properties of Industrially Produced Carbon Nanotube Yarns for Use in Structural Nanocomposites

Carbon nanotube synthesis and spinning as macroscopic fibers assisted by the ceramic reactor tube

Dry spinning yarns from vertically aligned carbon nanotube arrays produced by an improved floating catalyst chemical vapor deposition method

Graphene Interlocking Carbon Nanotubes for High-Strength and High-Conductivity Fibers.

Wet Twisting in Spinning for Rapid and Cost‐Effective Fabrication of Superior Carbon Nanotube Yarns

High-Strength Carbon Nanotube Fibers from Purity Control by Atomized Catalytic Pyrolysis and Alignment Improvement by Continuous Large Prestraining

Robust Carbon Nanotube Composite Fibers: Strong Resistivities to Protonation, Oxidation, and Ultrasonication

Enhancing Carbon Nanotube Yarns via Infiltration Filling with Polyacrylonitrile in Supercritical Carbon Dioxide

Super-strong CNT composite yarn with tight CNT packing via a compress-stretch process

Kinetic Modulation of Carbon Nanotube Growth in Direct Spinning for High-Strength Carbon Nanotube Fibers.

Strengthening Carbon Nanotube Fibers with Semi-Crystallized Polyvinyl Alcohol and Hot-Stretching

Carbon Nanotube Hollow Fiber Membranes: High-throughput Fabrication, Structural Control and Electrochemically Improved Selectivity