Relationship between the precipitation of face-centered cubic Zr2Ni phase and the stability of supercooled liquid state in Zr-Cu-Ni-Al metallic glasses : Special issue on bulk amorphous, nano-crystalline and nano-quasicrystalline alloys
Chunfei Li,Junji Saida,Akihisa Inoue
2000-01-01
Materials Transactions JIM
Abstract:The crystallization processes of (Zr 0.64 Ni 0.36 ) 100-x Al x (x = 5, 7.5 and 10) and (Zr 0.64 Ni 0.36-0.0x Cu 0.0x ) 95 Al 5 (x = 0, 6, 10, 13 and 16) metallic glasses were studied by using differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). For the (Zr 0.64 Ni 0.36 ) 100-x Al x (x = 5 and 7.5) and (Zr 0.64 Ni 0.36-0.0x Cu 0.0x ) 95 Al 5 (x = 0, 6, 10 and 13) alloys, crystallization proceeds through double-stage exothermic reactions. The first exothermic reaction corresponds to the precipitation of a metastable face-centered cubic Zr 2 Ni (F-Zr 2 Ni). For the (Zr 0.64 Ni 0.36 ) 100-x Al x (x = 10) and (Zr 0.64 Ni 0.36-0.0x Cu 0.0x ) 95 Al 5 (x = 16) alloys, crystallization proceeds through a single-stage exothermic reaction, corresponding to the precipitation of stable crystalline phases. Accompanying the above changes in crystallization mode, the supercooled liquid region ΔT x , defined as the temperature interval between the glass transition temperature Tg and the crystallization temperature T x , increases from 39 K for (Zr 0.64 Ni 0.36 ) 95 Al 5 to 64 K for the (Zr 0.64 Ni 0.36 ) 90 Al 10 in (Zr 0.64 Ni 0.36 ) 100-x Al x (x = 5, 7.5 and 10) alloy series, and from 39 K for (Zr 0.64 Ni 0.36 ) 95 Al 5 to 70 K for (Zr 0.64 Ni 0.20 Cu 0.16 ) 95 Al 5 in the (Zr 0.64 Ni 0.36-0.0x Cu 0.0x ) 95 Al 5 (x = 0, 6, 10, 13 and 16) alloy series. The reason for the stabilization of the supercooled liquid state at higher Al concentrations in the (Zr 0.64 Ni 0.36 ) 100-x Al x (x = 5, 7.5 and 10) alloy series and at higher Cu concentrations in the (Zr 0.64 Ni 0.36-0.0x Cu 0.0x ) 95 Al 5 (x = 0, 6, 10, 13 and 16) alloy series is discussed.