Abstract:Fe3O4@SiO2 particles were synthesized by a solvothermal method and a classical stOber method. Superparamagnetic Fe3O4 was the core, and a sol-gel coating of SiO2 was the shell. After the SiO2 surface was modified with amino groups, benzaldehyde was conjugated to the particles by a Schiff base reaction. The Fe3O4@SiO2 particles were emulsified in paraffin/water as a solid emulsifier to obtain an oil-in-water Pickering emulsion. After cooling the paraffin, the particles were fixed on the surface of the emulsion droplets. The particles were etched in ammonium fluoride aqueous solution, and Janus particles with different structures could be obtained by adjusting the etching time. Via the in situ growth of metal Pt or Ag nanoparticles, superparamagnetic Fe3O4@SiO2-Pt or Fe3O4@SiO2-Ag Janus particles were obtained. The movement of Fe3O4@SiO2-Pt Janus particles was observed due to the catalytic decomposition of hydrogen peroxide aqueous solution. It was found that in the short term, there was a linear motion, while in the long term, the motion direction and trajectory were random. Fe3O4@SiO2-Ag Janus particles were used as magnetic solid surfactants to stabilize the emulsions and catalyze the nitro reduction. About 60% of the surficial area of the Janus particles was modified by phenyl groups, while the remaining 40% was covered with Ag nanoparticles. Under the premise of maintaining the Janus balance, the whole particle became more hydrophobic, which was conducive to the formation of the water-in-oil emulsion. In addition, the Ag side of the Janus particles was towards the aqueous phase, and the opposite hydrophobic side was towards the oil phase. The Janus particles possessed a fixed orientation assembly at the oil-water interface. The assemble membrane possessed Janus characteristics, and it facilitated the stable dispersion of the emulsion and the catalysis. The method has the advantages of a simple principle, capability for mass production, universality and versatility. It is expected that Janus particles will be used to more precisely regulate the zoning with different functional substances.

Generation of Bifeo3-Fe3o4 Janus Particles Based on Droplet Microfluidic Method

Microfluidic synthesis of multiferroic Janus particles with disk-like compartments

Microfluidic Generation of Magnetoresponsive Janus Photonic Crystal Particles

Fabrication of tunable Janus microspheres with dual anisotropy of porosity and magnetism.

Biocompatible Janus microparticle synthesis in a microfluidic device

Emulsion Interfacial Synthesis of Polymer/Inorganic Janus Particles

Multifunctional Fe3O4@SiO2 Janus Particles

Amphiphilic Janus Particles Generated Via a Combination of Diffusion‐Induced Phase Separation and Magnetically Driven Dewetting and Their Synergistic Self‐Assembly

Microfluidic Generation of Magnetic-Fluorescent Janus Microparticles for Biomolecular Detection

Facile fabrication of Fe3O4@PS/PGMA magnetic Janus particles via organic–inorganic dual phase separation

Microfluidic Synthesis of Fe Nanoparticles

Janus and Ternary Particles Generated by Microfluidic Synthesis: Design, Synthesis, and Self-Assembly.

Design of Janus Particles by Bipolar Electrochemistry at the Water-Organic Interface

Facile Method for Large Scale Synthesis of Magnetic Inorganic-Organic Hybrid Anisotropic Janus Particles

Controllable Monodisperse Amphiphilic Janus Microparticles

Synthesis of Anisotropic Magnetic Polymeric Janus Particles by In Situ Separation of Magnetic Nanoparticles in a Microfluidic Device

Size-controlled Synthesis of BiFeO 3 Nanoparticles by a Facile and Stable Sol–gel Method

Synthesis of Janus Particles Via Strain-Driven Microphase Separation and Their Assembly into Nanoscale Vesicles.

Microfluidic generation of monodispersed Janus alginate hydrogel microparticles using water-in-oil emulsion reactant.

Generation of Janus alginate hydrogel particles with magnetic anisotropy for cell encapsulation.

Preparation of Monodispersed Hybrid Nanospheres with High Magnetite Content from Uniform Fe3O4 Clusters