Pressure Induced Increase of Particle Size and Resulting Weakening of Elastic Stiffness of Ceo2 Nanocrystals

ZW Wang,YS Zhao,D Schiferl,CS Zha,RT Downs

DOI: https://doi.org/10.1063/1.1768298

IF: 4

2004-01-01

Applied Physics Letters

Abstract:We demonstrate that the compressibility of cubic fluorite-structure CeO2 nanocrystals (10nm) increases at pressures above ∼20GPa. At ambient pressure, CeO2 nanocrystals exhibit larger cell parameters than micro-sized samples, and initially exhibit a higher bulk modulus of 328(12)GPa. However, above 20GPa, the bulk modulus is reduced to 230(10)GPa. Thus, a critical pressure of ∼20GPa was determined that signifies the onset of size-induced weakening of elastic stiffness in nanocrystalline CeO2. Comparison of the x-ray diffraction peaks widths between the platinum standard and CeO2 indicates that a significant increase of particle size in CeO2 appears at a pressure of ∼20GPa. It is suggested that the initial large value of the bulk modulus is a result of either an enhanced surface energy or from the pressure induced stiffness of Young’s modulus (E) and Poisson’s ratio (μ); while the weakening of the elastic stiffness above 20GPa is due to a pressure-induced increase of particle size.