Construction and Characterization of Pyrene-Alkyne Based Porous Frameworks
Zhang Tingting,Wang Haitao,Ma Heping,Sun Fuxing,Cui Xiaoqiang,Zhu Guangshan
DOI: https://doi.org/10.6023/a13060669
2013-01-01
Acta Chimica Sinica
Abstract:We report here a porous aromatic framework (PAF-27), which is constructed by a quadrilateral building block 1,3,6,8-tetraethynylpyrene with the linker 9,10-dibromoanthracene via Sonogashira-Hagihara coupling reaction. PAF-27 with plentiful phenyl rings in networks exhibits permanent porosity, high thermal and chemical stabilities, and excellent sorption abilities towards organic chemical pollutants at the saturated vapor pressure and room temperature. The structures of 1,3,6,8-tetrakis(4-(trimethylsilyl)ethynyl)pyrene, 1,3,6,8-tetraethynylpyrene and PAF-27 are firstly studied by H-1 NMR and C-13 CP/MAS NMR spectroscopy. As shown in the structure of PAF-27, all of the carbon signals with a chemical shift in the range of delta 120 similar to 140 are observed, which are related to aromatic carbon atoms of building phenylene. groups in the framework. Additionally, the structures with triple-bond linkages have been confirmed by the characteristic resonance of a triple-bonded carbon with a corresponding peak at around delta 90. IR spectra of initial monomer and final product can be found that the characteristic absorption peak for C-Br at 577 cm(-1) disappears, which gives an indication for the breakage of the C-Br bonds of 9,10-dibromoanthracene. In addition, the intense absorption peak associated with alkynyl C-H stretching vibration near 3280 cm(-1) from the terminal alkyne groups vanishes. Meanwhile, a peak with low intensity is observed near 2169 cm(-1) in the final product, which is assigned to the alkyne triple-bond stretching vibration mode. TGA analysis shows that PAF-27 is thermally stable up to 320 degrees C in air condition. In addition, the material also exhibits high chemical stability and cannot dissolve in any common organic solvents. N-2 sorption results reveal that the BET surface area of PAF-27 is 560 m(2)/g and the average pore size is about 0.63 nm. Because of the rich aromatic rings, the large BET and narrow pore distribution, it will display relatively high sorption abilities for gases.