Abstract:A high-quality dielectric layer is essential for organic thin-film transistors (OTFTs) operated at a low-power consumption level. In this study, a facile improved technique for the synthesis of solution-processed silica is proposed. By optimizing the synthesis and processing technique fewer pores were found on the surface of the film, particularly no large holes were observable after improving the annealing process, and the improved solution-gelation (sol-gel) SiOx dielectric achieved a higher breakdown strength (1.6 MV/cm) and lower leakage current density (10-8 A/cm2 at 1.5 MV/cm). Consequently, a pentacene based OTFT with a high field effect mobility (~1.8 cm2/Vs), a low threshold voltage (-1.7 V), a steeper subthreshold slope (~0.4 V/dec) and a relatively high on/off ratio (~105) was fabricated by applying a hybrid gate insulator which consisted of improved sol-gel SiOx and polyvinyl phenol (PVP). This could be ascribed to both the high k of SiOx and the smoother, hydrophobic dielectric surface with low trap density, which was proved by atomic force microscopy (AFM) and a water contact angle test, respectively. Additionally, we systematically studied and evaluated the stability of devices in the compressed state. The devices based on dielectric fabricated by conventional sol-gel processes were more susceptible to the curvature. While the improved device presented an excellent mechanic strength, it could still function at the higher bending compression without a significant degradation in performance. Thus, this solution-process technology provides an effective approach to fabricate high-quality dielectric and offers great potential for low-cost, fast and portable organic electronic applications.

Solution-processed small molecule transistors with low operating voltages and high grain-boundary anisotropy

Large-Dimensional Organic Semiconductor Crystals with Poly(butyl Acrylate) Polymer for Solution-Processed Organic Thin Film Transistors

Single-Step Solution Processing Of Small-Molecule Organic Semiconductor Field-Effect Transistors At High Yield

Fabrication and Characterization of Controllable Grain Boundary Arrays in Solution Processed Small Molecule Organic Semiconductor Films

Solution-grown Small-Molecule Organic Semiconductor with Enhanced Crystal Alignment and Areal Coverage for Organic Thin Film Transistors

Solvent Exchange in Controlling Semiconductor Morphology

Solution-Crystallized Organic Semiconductors with High Carrier Mobility and Air Stability

Small-molecule Additives for Organic Thin Film Transistors

Controlled growth of large-area high-performance small-molecule organic single-crystalline transistors by slot-die coating using a mixed solvent system.

Large-scale Fabrication of Field-Effect Transistors Based on Solution-Grown Organic Single Crystals

Poly(butyl Acrylate) Polymer Enhanced Phase Segregation and Morphology of Organic Semiconductor for Solution‐processed Thin Film Transistors

Facile Synthesis of Solution-Processed Silica and Polyvinyl Phenol Hybrid Dielectric for Flexible Organic Transistors

Solution-processed High Performance Organic Thin Film Transistors Enabled by Roll-to-roll Slot Die Coating Technique

Controlling Aggregation and Crystallization of Solution Processed Diketopyrrolopyrrole Based Polymer for High Performance Thin Film Transistors by Introducing Solvent Additive

Volatilize-controlled Oriented Growth of the Single-Crystal Layer for Organic Field-Effect Transistors.

Polyacrylate Polymer Assisted Crystallization: Improved Charge Transport and Performance Consistency for Solution-Processable Small-Molecule Semiconductor Based Organic Thin Film Transistors

Low-Voltage Organic Thin-Film Transistors with Improved Stability and Large Transconductance

Fabrication of Highly Oriented Large-Scale TIPS Pentacene Crystals and Transistors by the Marangoni Effect-Controlled Growth Method.

High Mobility Organic Transistors Fabricated from Single Pentacene Microcrystals Grown on a Polymer Film

Diketopyrrolopyrrole-based small molecules for solution-processed n-channel organic thin film transistors

Blending Crystalline/liquid Crystalline Small Molecule Semiconductors: A Strategy Towards High Performance Organic Thin Film Transistors