Abstract:Super- hydrophobic surfaces have attracted great research interest due to their novel performance as self-cleaning, anti-fog, and anti -oxidation. In this work,a new approach,based on elastomeric templates and UV-curable resins I has been developed to prepare super- hydrophobic surfaces. Poly( dimethylsiloxane) (PDMS, Sylgard 184) was purchased from Dow Coming and used to replicate lotus-leaf surfaces. In the replication step, PDMS blocks were prepared through replica molding against lotus-leaf surfaces. PDMS prepolymer was prepared by mixing the elastomer base and curing agent in a ratio of 10: 1. After 20 min, the PDMS prepolymer was poured into molds within fresh lotus-leaf surfaces as masters. Then the prepolymer was cured in 40 degrees C oven for 4 h. After curing and peeling off, the PDMS blocks with negative lotus-leaf surfaces' structures were obtained. Microscope observation indicates that the PDMS blocks' surfaces were featured with hollow cavities of 7 similar to 12 microns in diameter. The PDMS blocks could be used as stamps in the following curling step of ultraviolet (UV)-curable prepolymers, which consist of oligomer,cross-linking agent, reactive monomer, and photo- initiator. In the experiment, isobomyl acrylate, siliconized urethane acrylate, benzoin dimethyl ether and dipentaerythritol pentaacrylate were used as monomer, oligomer, photoinitiator and crosslinking agent, respectively. In a typical process, UV-curable prepolymer was prepared by mixing monomer, oligomer, photoinitiator and crosslinking agent in a ratio of 10: 68: 2: 20. Then the prepolymer was put into a 0. 085 MPa vacuum oven to remove air bubble. The prepolymer was spread on substrates ( silicon wafer or glass slide), pressed by the PDMS stamp with replicated lotus-leaf surface. Finally, the UV-curable prepolymer covered with the PDMS stamp was exposed to UV-light (500 mu W/cm(2) After curing for 15 min, the PDMS stamp was peeled off, and the cured sample was store in 40 degrees C oven for 5 h before further experiments. Measured by scanning electron microscopy ( SEM, Hitachi S-4500), a large amount of papillary microstructures with an average diameter of about 7 - 10 microns and average height of 10 similar to 18 microns could be seen on the surfaces. These papillary microstructures are replicas of the surface patterns of the lotus leaves. The obtained surfaces had water contact angles larger than 150 degrees and small sliding angles, exhibiting fascinating super- hydrophobicity like lotus-leaf surfaces. Obviously, the replicated papillary microstructures played important role in the increase of surface hydrophobicity from about 105 degrees (smooth film surface) to 157 degrees. This result can be explained with the Wenzel theory. Factors influencing the wettability of resulted surfaces, such as content of monomer, cross-linking agent, initiator and light irradiation time, were also studied in detail. Experiments showed that the surface contact angles increase with the content of photoinitiator before 0. 7 % and decrease with the content of crosslinking agent when larger than 20 % A monomer content of about 10% and irradiation time longer than 10 min were also preferable for achieving high hydrophobicity. Combining the advantages of soft- I lithographic and UV-curing techniques, this approach can be potentially applied in fabrication of large-area super- hydrophobic surfaces.

Engineering Superlyophobic Surfaces On Curable Materials Based On Facile And Inexpensive Microfabrication

Facile and Versatile Replication of High-Performance Superlyophobic Surfaces on Curable Substrates Using Elastomer Molds

Fabrication of Flexible and Re-entrant Liquid-Superrepellent Surface Using Proximity and PNIPAM-Assisted Soft Lithography

Superhydrophobic Surfaces Fabricated by Replica Molding and Its Applications

PREPARATION OF SUPER-HYDROPHOBIC SURFACES BY USING ELASTOMER TEMPLATES AND UV-CURABLE RESIN

Robust and Stable Transparent Superhydrophobic Polydimethylsiloxane Films by Duplicating Via a Femtosecond Laser-Ablated Template

Fabrication of Flexible and Reentrant Liquid-Superrepellent Surfaces Enabled by Proximity and Soft Lithography

Further resources for molecular protocols in Salmonella research.

Construction of superhydrophobic surfaces via dual-scale modified particles and digital light processing 3D printing techniques

Super-Hydrophobic PDMS Surface with Ultra-Low Adhesive Force

Slippery Liquid-Attached Surface for Robust Biofouling Resistance

Multifunctional Superhydrophobic Surfaces Templated from Innately Microstructured Hydrogel Matrix

Design and Synthesis of Robust Superhydrophobic Coating Based on Epoxy Resin and Polydimethylsiloxane Interpenetrated Polymer Network

Transparent and Robust Superhydrophobic Structure on Silica Glass Processed with Microstereolithography Printing

Sustainable and Practical Superhydrophobic Surfaces via Mechanochemical Grafting

Serum prolactin in epilepsy and hysteria.

Large-Area Preparation of Robust and Transparent Superomniphobic Polymer Films.

Large-Area Preparation of a Robust Superamphiphobic Coating for Chemical Mechanical Polishing Application

Simple Design for Durable and Clear Self-Cleaning Coatings

Large‐Scale, Abrasion‐Resistant, and Solvent‐Free Superhydrophobic Objects Fabricated by a Selective Laser Sintering 3D Printing Strategy

Fabrication of Polymethyl Methacrylate (PMMA) Hydrophilic Surfaces Using Combined Offset-Tool-Servo Flycutting and Hot Embossing Methods