Abstract:To achieve the high dispersion of SiO2 nanoparticles in polyurethane acrylate resin, the titanate coupling agent, PN-102, was used as the surface modifier to prepare the modified SiO2 nanoparticles (Si-PN102-5) with small particle size and good dispersion ability in PUA-6 resin. Accordingly, hydrophilic SiO2 (Si-380) and hydrophobic SiO2 (Si-115) were introduced into PUA-6 resin to prepare the corresponding composite coatings, so as to investigate the effects of SiO2 nanoparticles modified with different surface modifiers on the properties of PUA / SiO2 composite coatings. The properties of PUA / SiO2 composite coatings were characterized by the tests of FTIR, AFM, SEM, DMA, TG and so on. The FT-IR and XPS results show that PN-102 had functionalized the SiPN102-5 particle surface successfully. The TEM test displays that the particle size of SiO2 was almost unchanged before and after modification, maintaining at about 20-30 nm. The SEM, DMA and tensile test reveal that Si-PN102-5 not only blocks the interaction and accumulation of nanoparticles, but also enhances the interface interaction with polymer chains through chain entanglement, which endows Si-PN102-5-5% composite coatings with highest mechanical strength among the other prepared coatings, reaching to 11.0 +/- 0.1 MPa in tensile strength and 9.4 +/- 3.0% in elongation at break. The pencil hardness of the prepared Si-PN102-5-5% composite coating could reach to 5H which is higher than the commercial PUA-6 based coating, and it also displayed good adhesion (4B) and flexibility (3 mm). The TG results show that all of prepared composite coatings display good thermal stability with a decomposition temperature of higher than 250 degrees C.

The Utilization of Carbon Nitride to Reinforce the Mechanical and Thermal Properties of UV-curable Waterborne Polyurethane Acrylate Coatings

The Coating Properties of Waterborne UV-Curable Polyurethane Acrylate and Influencing Factors

Preparation and properties of UV-curable waterborne graphene oxide/polyurethaneacrylate composites

A novel nanosilica-reinforced waterborne UV-curable material

Preparation and Properties of UV-Curable Waterborne Polyurethane Acrylate/MXene Nanocomposite Films

Preparation and Properties of Multifunctional Waterborne Polyurethane Acrylate/Nanosilica Hybrid Materials

Preparation and Properties of UV-curable Diamine-Based Polyurethane Acrylate Hard Coatings

Preparation and Properties of UV-curable Polyurethane Acrylate/sio2 Composite Hard Coatings

Preparation and Mechanical Properties of Waterborne Polyurethane/Carbon Nanotube Composites

Improving the Performance of UV-curable Coatings with Carbon Nanomaterials

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Preparation and properties of novel UV-curable waterborne epoxy and acrylate modified polyurethane

Preparation of UV-cured polyurethane-urea acrylate coatings with high hardness and toughness

Preparation of functional ZnO nanoparticles and their application as UV photosensitizer and reinforcing agent for waterborne polyurethane acrylate composite coating

Modified Ultraviolet-Curable Water Dispersible Polyurethane-Acrylates

Characterization and Properties of UV-Curable Hyperbranched Polyurethane Acrylate-Polyurethane Diacrylate/SiO2 Hybrid Coatings

Synthesis of a Novel UV Crosslinking Waterborne Siloxane–polyurethane

Optimization of UV-Curable Polyurethane Acrylate Coatings with Hexagonal Boron Nitride (hBN) for Improved Mechanical and Adhesive Properties

Preparation of Uv-Curable Functionalized Graphene/Polyurethane Acrylate Nanocomposite with Enhanced Thermal and Mechanical Behaviors

Synthesis and Properties of Cationic Core-Shell Fluorinated Polyurethane Acrylate

Novel Waterborne UV-Curable Hyperbranched Polyurethane Acrylate/Silica with Good Printability and Rheological Properties Applicable to Flexographic Ink