Preparation and Properties Study of G-POSS/EP Hybrid Materials
JIAO Jian,LIU Peng,CAI Yu,WU Guang-li
DOI: https://doi.org/10.3969/j.issn.1005-5770.2012.11.006
2012-01-01
Abstract:With triethylene tetramine(TETA)as curing agent,glycidyl ether polyhedral oligomeric silsesquioxanes/epoxy resin(G-POSS/EP)was prepared by blending method.The influence of G-POSS in curing reaction,dielectric property,mechanical properties and thermal property of hybrid materials was studied,and the microstructure and properties of hybrid materials were characterized and analyzed.The results showed that with the introduction of G-POSS the reactivity of EP improved,the transparency was favorable,the mechanical properties and dielectric properties of hybrid materials all improved.The dielectric property,mechanical strength and rigidity of the hybrid materials increased more obviously when the mass ratio of m(G-POSS)∶m(EP)was 20∶100 and the fracture surface was ductile fracture.The tensile strength,elongation at break and bend strength of G-POSS/EP materials were 67.8 MPa,3.44% and 116.7 MPa,compared with pristine epoxy,they were increased by 83.20%,320.13%,49.17%,respectively.