Picosecond laser generation of Ag–TiO 2 nanoparticles with reduced energy gap by ablation in ice water and their antibacterial activities

Abubaker Hamad,Lin Li,Zhu Liu,Xiang Li Zhong,Tao Wang
DOI: https://doi.org/10.1007/s00339-015-9111-6
2015-01-01
Applied Physics A
Abstract:Ag–TiO 2 nanoparticles were synthesised in ice water using a picosecond laser with a 1064-nm wavelength, at a 200-kHz repetition rate, a laser pulse energy of 42–43.79 µJ, and laser fluences of 0.342–0.357 J/cm 2 , by ablation of solid Ag and Ti targets. The absorption spectra and size distribution of the colloidal nanoparticles were obtained by UV–Vis spectroscopy and transmission electron microscopy, respectively. The morphology and chemical composition of the nanoparticles were characterised using high-angle annular dark-field-scanning transmission electron microscope and energy-dispersive X-ray spectroscopy. The results show that the sizes of the Ag–TiO 2 nanoparticles range from less than 10–130 nm, with some large particles above 130 nm, of which the predominant size is 20 nm. A significant reduction in the energy gap of TiO 2 nanoparticles was obtained to 1.75 eV after the modification with Ag nanoparticles during co-ablation. The role of Ag nanoparticles in the reduction in the energy band gap of the TiO 2 nanoparticles can only be seen during laser ablation in an ice environment but not in deionised water at room temperature. Furthermore, the TiO 2 nanoparticles were produced in ice and deionised water under the same laser and experimental conditions; the results show that the nanoparticles in both media have the same energy gap (about 2.4 eV). The antibacterial activity of the Ag–TiO 2 nanoparticles generated was then tested against E. coli bacteria under standard laboratory light conditions. The results show that the nanoparticles can effectively kill E. coli bacteria much more effectively than laser-generated TiO 2 nanoparticles.
What problem does this paper attempt to address?