Abstract:The purpose of this study was to examine the microstructure and texture evolution of a twin roll cast AZ31 magnesium alloy after multi-pass warm rolling in a temperature range from 233 to 248 degrees C. Reduction per pass was kept constant at about 10% and the total reduction was 98.2% after 33 pass steps with a change of sheet thickness from initially 2.85 min down to 50 mu m. The rolled sheets exhibited a fairly strong basal texture with an intensity of 17-21 multiples of random distribution (MRD) in the initial stages (with a thickness above 0.47 mm) due to the lower rolling temperatures. The basal texture intensity decreased to 13-15 MRD in the later stages (with a thickness below 0.3 mm) due to the occurrence of dynamic recrystallization at slightly higher rolling temperatures to balance out the demand of rolling force. The basal pole in the thicker sheets spread slightly along +/- TD with an ellipse shape mainly due to the activation of < a > prismatic slip and the occurrence of shear bands, while the splitting of basal pole in the thinner sheets was observed to be along the RD with a tilting angle of about +/- 10 degrees. This was attributed to the activation of < a + c > pyramidal slip. The average grain size in the thinner sheets in the later stages during the multi-pass rolling decreased almost linearly with increasing number of rolling steps. This could be explained via a change in the Zener-Hollomon parameter which was associated with the strain rate affected by the sheet thickness during rolling at a constant percent reduction. (C) 2015 Elsevier B.V. All rights reserved.

Effect of the Final Rolling Speeds on the Stretch Formability of AZ31 Alloy Sheet Rolled at a High Temperature

Effect of Final Rolling Temperature on Microstructures and Mechanical Properties of AZ31 Alloy Sheets Prepared by Equal Channel Angular Rolling and Continuous Bending

Effect of Final Rolling Speed on Microstructure and Performance of AZ31 Magnesium Alloy Sheet under Small Strain Condition

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Influence of Rolling Temperature on Microstructure and Tensile Properties of AZ31 Sheets

Effect of Asymmetric Cross Rolling on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Effect of Rolling Parameters on Room-Temperature Stretch Formability of Mg–2Zn–0.5Ca Alloy

Texture Evolution of AZ31 Magnesium Alloy Sheets During Warm Rolling

Mechanical Properties and Texture Evolution During Rolling Process of an AZ31 Mg Alloy

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Effects of Hot Rolling Processing on Microstructures and Mechanical Properties of Mg–3%Al–1%Zn Alloy Sheet

Microstructure and properties of AZ31 alloy by static recrystallisation at lower temperature

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Annealing Behavior Of Rolled Az31 Alloy Sheet

Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys

Grain refining and improving mechanical properties of AZ31 Mg alloy sheets by multi-pass warm rolling with falling temperature

The effect of grain size on texture evolution and mechanical properties of an AZ31 magnesium alloy during cold-rolling process

Effect of Deformation Temperature on Texture and Mechanical Properties of ZK60 Magnesium Alloy Sheet Rolled by Multi-Pass Lowered-Temperature Rolling

Enhancement of Tensile Ductility and Stretch Formability of AZ31 Magnesium Alloy Sheet Processed by Cross-Wavy Bending

Effect of Single-Pass Rolling on Microstructure and Mechanical Properties of AZ31 Alloy Processed by Equal Channel Angular Pressing