Structural, morphological and multiferroic properties of the hydrothermally grown gadolinium (Gd) and manganese (Mn) doped sub-micron bismuth ferrites

ping tang,daihong kuang,shenghong yang,yueli zhang

DOI: https://doi.org/10.1016/j.jallcom.2015.10.010

IF: 6.2

2016-01-01

Journal of Alloys and Compounds

Abstract:Pure BiFeO3 and Gd, Mn doped BiFeO3 particles were synthesized with a hydrothermal method in a reaction solution containing a mineralizer of KOH. The products were characterized by X-ray diffraction, scanning electron microscope, transmission electron microscope, Raman spectroscopy, physical property measurement system and ferroelectric test system. Rietveld refinement and Raman spectra results reflect that the Gd, Mn doped samples undergo compositional-driven phase transition from rhombohedral to orthorhombic. Selected area electron diffraction and high-resolution transmission electron microscopy confirm the single-crystalline nature of our as-prepared samples. Compared with the linear magnetization-magnetic field relation in pure BiFeO3 particles, a clear hysteresis M-H loop can be observed in the Bi0.9Gd0.1FeO3 sample, which is ascribed to distorted spin cycloid and the magnetically active characteristic of Gd3+. Enhanced ferroelectric properties and reduced leakage current density were obtained in BiFe0.9Mn0.1O3 and Bi0.9Gd0.1Fe0.9Mn0.1O3. The leakage current density of the BiFe0.9Mn0.1O3 and Bi0.9Gd0.1Fe0.9Mn0.1O3 was reduced by two orders of magnitude as compared to that of pure BiFeO3. (C) 2015 Elsevier B.V. All rights reserved.