Abstract:xLi(2)MnO(3)center dot(1 - x)LiCoO2 (x = 0, 0.02, 0.05, 0.1) as a cathode material for lithium ion batteries has been prepared by a spray-drying assisted solid-state method. The effects of Li2MnO3 content on crystal structure, morphology, and high-voltage electrochemical performance of LiCoO2 have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and galvanostatic charge-discharge test. XRD results reveal that all samples have a well-ordered layered structure. SEM and EDS analyses confirm that homogeneous powders with a primary particle size of about 2 mu m are observed and the elementals distribute uniformly in the particles. Electrochemical tests demonstrate that the modified samples exhibit obviously enhanced cycling stability in the voltage ranges of 3.0-4.5 V and 3.0-4.6 V, although they deliver somewhat lower discharge capacity. Specifically, 0.02Li(2)MnO(3)center dot 0.98LiCoO(2) delivers the initial discharge capacity of 189.0, 216.8 mA h g (1) at 0.1 C in the voltage range of 3.0-4.5 V and 3.0-4.6 V, respectively, and excellent cycling behaviors at 1 C are achieved. (C) 2014 Elsevier B.V. All rights reserved.

Synthesis of Li2MnO3-stabilized LiCoO2 Cathode Material by Spray-Drying Method and Its High-Voltage Performance