Modification of the Α-Ti Laths to Near Equiaxed Α-Ti Grains in As-Sintered Titanium and Titanium Alloys by a Small Addition of Boron

Y. F. Yang,M. Yan,S. D. Luo,G. B. Schaffer,M. Qian
DOI: https://doi.org/10.1016/j.jallcom.2013.07.097
IF: 6.2
2013-01-01
Journal of Alloys and Compounds
Abstract:A small addition of boron (B) changes the morphology of the alpha-Ti laths in as-sintered Ti-6Al-4V and Ti-10V-2Fe-3Al to near equiaxed alpha-Ti grains and increases the number density of the resulting a-Ti grains by up to six folds. TiB forms at about 700 degrees C during heating to the isothermal sintering temperature and more than 90% of the TiB particles were found inside the a-Ti grains. Transmission electron microscopy (TEM) was used to identify the orientation relationships (ORs) between the TiB and alpha-Ti phases. Their exact ORs are affected by both the chemistry of the alloy and the processing conditions. The modification of the alpha-Ti laths and the substantial increase in the number density of the alpha-Ti grains are attributed to the enhanced heterogeneous nucleation of alpha-Ti on TiB due to the identified specific ORs and excellent lattice matches between these two phases. In addition, there exists a unique peritectoid reaction between beta-Ti and TiB during the subsequent cooling after isothermal sintering by which beta-Ti + TiB -> alpha-Ti, which may have contributed to the enhanced heterogeneous nucleation of a-Ti on TiB. (C) 2013 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?