Abstract:Upconversion luminescence (UCL) is a fluorescence process where two or more lower-energy photons convert into a higher-energy photon. Lanthanide (Ln3+)-doped UCL materials often suffer from weak luminescence, especially when directly synthesized by a hydrothermal (HT) process due to the existing hydroxyl group and undesirable arrangement of dopants within host lattices which quench luminescence and limit energy transfer. Therefore, additional heat treatment processes are required to enhance their UCL emission, even though direct hydrothermal synthesis without further heat treatment has the advantages of low energy consumption, fast synthesis, and wide applicability to generate UCL materials. In this study, via a HT process without annealing, we have produced Yb3+ and Er3+ co-doped SrMoO4 submicron spindles with a strong green UCL emission which can be seen with the naked eye, which HT produced oxide-based UCL materials often fail to demonstrate. We have investigated different HT synthesis conditions, such as temperature, time, pH and dopant composition, which control the nucleation, growth, lattice structure arrangement, and ultimately their UCL properties through XRD, SEM, EDS and UCL measurements. The bright green UCL from the SrMoO4:Yb,Er submicron spindles is further enhanced by post-synthesis annealing within a molten NaNO3/KNO3 system to prevent particle size growth. The green UCL intensity from the annealed SrMoO4:Yb,Er submicron spindles surpasses samples produced by the solid-state method and is comparable to that from the commercial NaYF4:Yb,Er sample. We have further studied the temperature-dependent luminescence of both the HT-prepared and molten-salt annealed SrMoO4:Yb,Er submicron spindle samples. The strong UCL from our SrMoO4:Yb,Er submicron spindles could warrant their candidacy for bioimaging and anticounterfeiting applications.

Anomalous Upconversion Luminescence of SrMoO4:Yb3+/Er3+ Nanocrystals by High Excited State Energy Transfer

Up-conversion luminescence of Er2Mo4O15 under 980 and 1550 nm excitation

Investigation of Anomalous Upconversion Luminescence in YbAG: Er, Mo

Upconversion Luminescence of Yb3+/Tb3+/Er3+-Doped Fluorosilicate Glass Ceramics Containing Srf2 Nanocrystals

Strong green upconversion emission from submicron spindle-shaped SrMoO4:Yb3+,Er3

Generalized Synthesis of NaLn(MoO4)2 Nano/microcrystals (ln = La–Lu and Y): the Effects of Lanthanide Contraction, Structure, and Down-/Up-conversion Luminescence

Intense Upconversion Luminescence of Er3+/Yb3+ Codoped Oxyfluoride Borosilicate Glass Ceramics Containing Ba2GdF7 Nanocrystals

Upconversion Luminescence Properties of Y 2 O 2 S:Er 3+ @Y 2 O 2 S:Yb 3+ ,tm 3+ Core-Shell Nanoparticles Prepared Via Homogeneous Co-Precipitation

Blue Upconversion of Tm3+ Using Yb3+ As Energy Transfer Bridge under 1532 Nm Excitation in Er3+, Yb3+, Tm3+ Tri-Doped CaMoO4

Highly efficient upconversion luminescence in narrow-bandgap Y2Mo4O15

Upconversion Luminescence Properties of Y2Mo4O15: Yb3+, Er3+ by Solid State Combustion Method.

Near-infrared to visible upconversion in Er 3+ and Yb 3+ codoped Lu 2O 3 nanocrystals: Enhanced red color upconversion and three-photon process in green color upconversion

The preparation of Y;O;:Er,Yb nanocrystals and study on luminescence properties of visible and infrared emission

Full-color Up-Conversion Emission from the Molybdate of Yb1.98Ln0.02Mo4O15 (ln=er, Ho, Tm)

Synthesis and Characterization of High-Efficiency Nanocrystal Up-Conversion Phosphors: Ytterbium and Erbium Codoped Lanthanum Molybdate

The upconversion luminescence properties of the Yb 3+ –Ho 3+ system in nanocrystalline Y 2 O 2 S

The dynamic variation of upconversion luminescence dependent on shell Yb3+ contents in NaYF4: Yb3+,Tm3+@NaYF4: Yb3+,Er3+ nanoparticles

Photoluminescence Properties of SrMoO4:Eu3+, Sm3+ Nanophosphors Prepared by Sol-Gel Method

Energy Transfer to Enhance the Characteristics Emission from Lanthanide-Doped Nanocrystals

The upconversion luminescence properties of the Yb<sup>3+</sup>–Ho<sup>3+</sup> system in nanocrystalline Y<sub>2</sub>O<sub>2</sub>S

Upconversion Photoluminescence Properties of SrY2O4:Er3+,Yb3+ under 1550 and 980 Nm Excitation