Abstract:Eu3+‐doped CaMoO4 nanophosphor was prepared using the solid‐state reaction technique. The influence of the PO42− group on the luminescence features of CaMoO4:Eu3+ was examined. Basic energy transfer mechanisms of CaMoO4:Eu3+ red emission were plotted. The influence of the PO42− group was examined in finding the best red color emission candidates for white‐LED devices. To investigate the impact of PO43− anionic groups, the trivalent europium ion‐doped calcium molybdate (CaMoO3‐PO4:xEu3+, where x = 0.5, 1.0, 1.5, 2.0, and 2.5 mol%) phosphors were synthesized using the solid‐state reaction method. The detailed study of the phosphor materials was carried out by X‐ray diffraction (XRD), field emission scanning electron microscopy (FE‐SEM), Fourier transform infrared spectroscopy (FT‐IR), X‐ray photoelectron spectroscopy (XPS), optical diffuse reflectance spectroscopy (DRS), and photoluminescence (PL) spectroscopy. The XRD results indicate that the substitution of PO43− anion and Eu3+ dopant ion did not affect the crystal structures of the CaMoO4 phosphors. Ultraviolet–visible (UV–vis) absorption analysis revealed the change of absorption edge of both un‐doped and Eu3+‐doped CaMoO4‐PO4 phosphors. Under the 394 nm UV‐excitation, the recorded PL spectra showed an intense peak at 615 nm corresponding to the Eu3+: 5D0 → 7F2 transition. The results of the Commission Internationale de l'Eclairage (CIE) diagram reported that the color of the emissions lies in the red color zone and there is no change in the CIE coordinates of the overall emission for Eu3+‐doped CaMoO4‐PO4 as Eu concentration changes. Thus, these observations led to finding the best red components for white light‐emitting diode applications.

Hydrothermal Synthesis and Luminescence Properties of 3D Walnut-Like CaMoO4:Eu3+ Red Phosphors

Low temperature synthesis and photoluminescent properties of CaMoO4:Eu3+ red phosphor with uniform micro-assemblies

Preparation of CaMoO_4:Eu~(3+) Micro/nanophosphors Via a Facile Hydrothermal Route and Their Photoluminescence Properties

Luminescent properties and synthesis of CaMoO4∶Eu3+ red phosphor by NH4Cl flux

Co-precipitation synthesis and photoluminescence properties of (Ca 1-x-y,Lny)MoO4: XEu3+ (Ln = Y, Gd) red phosphors

Self-assembled CaMoO4 and CaMoO4:Eu3+ Hierarchical Superstructures: Facile Sonochemical Route Synthesis and Tunable Luminescent Properties

Hydrothermal Synthesis and Spectral Properties of NaEu(MoO4)2 Red Submicro-Phosphors

Luminescence Investigation of Eu~(3+)-Bi~(3+) Co-Doped CaMoO_4 Phosphor

Enhanced Red Emission in Lithium Doped CaWO<sub>4</sub>:Eu<sup>3+</sup> and CaMoO<sub>4</sub>:Eu<sup>3+</sup> Phosphor

Enhanced Red Emission in Lithium Doped CaWO 4 :Eu 3+ and CaMoO 4 :Eu 3+ Phosphor

Low temperature microwave solid-state synthesis of red-emitting CaMoO4:Eu3+, Li+ phosphors with controlled morphology

[Synthesis of the CaCO3:Eu3+ Red Phosphor by Microwave Method].

Solid-state Synthesis, Characterization and Luminescent Properties of Eu3+-doped Gadolinium Tungstate and Molybdate Phosphors: Gd(2−x)MO6:Eux3+ (M=W, Mo)

Photoluminescence characterization of a novel red-emitting phosphor In 2 (MoO 4 ) 3 :Eu 3+ for white light emitting diodes

Synthesis and Characteristic of Camoo4:Eu3+ Red Phosphor for W-Led by Co-Precipitation

Preparation and characterization of Eu 3+ -doped CaCO 3 phosphor by microwave synthesis

Close-Relationship Between the Luminescence and Structural Characteristics in Efficient Nanophosphor Y2mo4o15:Eu3+

Structure and Luminescent Properties of CaCO3:Eu3+ Phosphors Prepared in Ethylene Glycol-Water Mixed Solvent

Luminescent Properties of Lu2MoO6:Eu3+ Red Phosphor for Solid State Lighting

Investigation of red‐emitting CaMoO4: Eu3+ phosphor by partitioning of substitutional PO43− ions via solid‐state reaction method

Synthesis and characterization of CaMoO4:Eu3+ @ TiO2 red phosphors