Abstract:A series of thermoresponsive core-shell microgels were synthesized using SiO2 as core and hybrid gel (hyaluronate/poly(N-isopropylacrylamide) (HA/PNIPAm)) as shell. SiO2 particles were modified by KH550 to get -NH2 groups, which could be protonized in acid condition. So that they could be covered by HA chains through electrostatic force. Then, HA was grafted using glycidyl methacrylate (GMA) to obtain C=C groups for the next synthesis of 1.1261/PNIPAm hybrid gel. The modification degree of C=C was determined through H-1 nuclear magnetic resonance spectroscopy (H-1 NMR). Fourier-transform infrared spectra (FT-IR) were used to monitor each synthesis step. Transmission electron microscopy (TEM) images showed that SiO2-HA/PNIPAm microgels were almost monodispersed and possessed perfect core-shell structures. Thermoresponsive behaviors of microgels were investigated using micro-differential scanning calorimetry (Micro-DSC), which showed that the lower critical solution temperature (LCST) values were almost the same, around 34 +/- 0.1 degrees C, regardless of the synthetic parameters. The thixotropy of SiO2-HA/PNIPAm microgels was studied using rheometer. It turned out that the microgels possessed negative thixotropy. Moreover, when the temperature was higher than LCST, the thixotropy was better than that of lower temperature. The swelling behaviors of SiO2-HA/PNIPAm microgels were evaluated by combining experiment methods and theoretical calculation. Dynamic light scattering (DLS) was used to analyze the swelling behavior of microgels with the increase of temperature. The DLS results showed that microgels possessed good thermoresponsive behavior with a LCST at about 34 which was in accordance with that determined by Micro-DSC. The hydrodynamic diameter (d) was found to be dependent on the size of core, the Ad, of HA and the amount of PNIPAm. Theoretical calculation was carried out using a lattice molecular thermodynamic model based on our previous works, it showed that the calculated results were in good agreement with the experimental data. The results indicated that the model could predict the swelling behavior of thermoresponsive core-shell structured microgel using fewer model parameters. This work will provide fundamental reference for further research.

Synthesis and Swelling Behavior of Sio2-Ha/Pnipam Core-Shell Structured Thermoresponsive Microgels

Synthesis and Volume Phase Behaviors of Temperature-Sensitive PNIPAM-HA-MSiO2 Core-Shell Hybride Microgels

Synthesis and characterization of thermoresponsive and biocompatible core–shell microgels based on N-isopropylacrylamide and carboxymethyl chitosan

Thermoresponsive behavior and rheology of SiO2–hyaluronic acid/poly(N‐isopropylacrylamide) (NaHA/PNIPAm) core–shell structured microparticles

Thermosensitive ionic microgels via surfactant-free emulsion copolymerization and in situ quaternization cross-linking.

Synthesis and Characterization of PNIPAM Microgel Core–silica Shell Particles

Preparation and properties of thermo-sensitive organic/inorganic hybrid microgels

Thermo-sensitive ionic microgels via post quaternization cross-linking: fabrication, property, and potential application

Synthesis and Properties of Organic-Inorganic Hybrid P(Nipam-Co-Am-Co-Tmspma) Microgels

Preparation and characterization of temperature and pH responsive core-shell microgel

Synthesis and Characterization of Poly(n-Isopropylacrylamide-co-n,n′-methylenebisacrylamide-co-acrylamide) Core – Silica Shell Nanoparticles by Using Reactive Surfactant Polyoxyethylene Alkylphenyl Ether Ammonium Sulfate

Schizophrenic Core-Shell Microgels: Thermoregulated Core and Shell Swelling/Collapse by Combining Ucst and Lcst Phase Transitions

SYNTHESIS OF GLUCOSE-SENSITIVE CORE-SHELL MICROGELS

P(NIPAm-co-TMSPMA)/Silica Hybrid Microgels: Structures, Swelling Properties and Applications in Fabricating Macroporous Silica

Preparation Of Submicrometer-Sized Monodispersed Thermoresponsive Core-Shell Hydrogel Microspheres

Preparation and Characterization of Thermosensitive Organic–inorganic Hybrid Microgels with Functional Fe3O4 Nanoparticles As Crosslinker

Preparation and characterization of poly(N-isopropylacrylamide)-polyethylene glycol core-shell microgel

Preparation of thermoresponsive core–shell polymeric microspheres and hollow PNIPAM microgels

Thermosensitive hybrid hydrogels with silica nanoparticle-cross-linked polymer networks

Thermo-responsive Hollow Silica Microgels with Controlled Drug Release Properties.

Fabrication and characterization of microgel-impregnated, thermosensitive PNIPAAm hydrogels