Synthesis and Characterization of Coumarin-Containing Hyperbranched-Star Copolymers

Fan Wei,Li Min,Hong Chunyan,Pan Caiyuan

DOI: https://doi.org/10.6023/a14120897

2015-01-01

Acta Chimica Sinica

Abstract:Coumarin-containing inimer was prepared and used in the self-condensing vinyl polymerization (SCVP) of 2-(2-methoxyethoxy)ethyl methacrylate (MEO(2)MA). The molar ratio of inimer/MEO(2)MA was set as 1 7, and the reaction was carried out at 50 degrees C for 80 h to afford hyperbranched poly(2-(2-methoxyethoxy)ethyl methacrylate) (H-PMEO(2)MA). The molecular,weight of H-PMEO(2)MA is 5400 g/mol and M-w/M-n is 1.56. The content of coumarin group in the hyperbranched polymer is consistent with the feed ratio. Then the resultant H-PMEO(2)MA was used as macroinitiator in the following atom transfer radical polymerization (ATRP) of dimethylaminoethyl methacrylate (DMAEMA), and thermo-responsive hyperbranched-star copolymers with different molecular weights were achieved. NMR and GPC were utilized to characterize the hyperbranched-star copolymers. Lower critical solution temperature (LCST) of H-PMEO2MA is below room temperature, thus the hyperbranched-star copolymers can self-assemble to form micelles in water at room temperature. TEM and DLS were utilized to characterize the morphology and size of the micelles. Coumarin group has the potential to photodimerize via a cycloaddition to form a cyclobutane ring under irradiation of UV light at lambda>310 rim, and the dimer can be reversibly divide into two coumarin groups under irradiation of UV light at lambda<260 nm. In this case, when exposed to irradiation of UV light at lambda=320 nm, the micelles were core-crosslinked via photodimerization of the coumarin groups. This procedure has been monitored by the UV-Vis spectrum. With increasing irradiation time, the absorbance of coumarin group at 320 rim decreased. After 30 min, the absorbance almost disappeared, indicating that most of coumarin groups dimerized. Under irradiation at lambda=254 rim, de-crosslinking reaction of the crosslinked micelles occurred, with the division of dimer into two coumarin groups. During the self-assembly, Nile Red as the model drug was loaded, and the release of Nile Red under different conditions was investigated. When placed at 25 degrees C, both core cross-linked and uncross-linked micelles exhibit a relatively slow release behavior, which suggest the good stability of the micelles. While at 0 degrees C, a burst release of the uncross-linked micelles was observed due to the disassembling of micelles. However, the morphology of core cross-linked micelles was kept well, and only a small amount of Nile Red was released.