First-Principles Investigation of Thermodynamic, Elastic and Electronic Properties of Al3v and Al3nb Intermetallics under Pressures
Zhe Chen,Peng Zhang,Dong Chen,Yi Wu,Mingliang Wang,Naiheng Ma,Haowei Wang
DOI: https://doi.org/10.1063/1.4913664
IF: 2.877
2015-01-01
Journal of Applied Physics
Abstract:The thermodynamic, elastic, and electronic properties of D022-type Al3V and Al3Nb intermetallics were studied using the first-principle method. The results showed the pressure has profound effects on the structural, mechanical and electronic properties in both Al3V and Al3Nb. Thermodynamically, the formation enthalpies for Al3V and Al3Nb were derived, which agreed well with available experimental and theoretical values. Comparably, Al3Nb was a more stable phase with the more negative Hf than Al3V. Mechanically, the calculated elastic constants showed linearly increasing tendencies, and satisfied the Born's criteria from 0–20 GPa, indicating the mechanically stability of Al3V and Al3Nb under this pressure range. Further, the mechanical parameters (i.e., bulk modulus (B), shear modulus (G), and Young's modulus (E)) were derived using the Voigt-Reuss-Hill (VRH) method, and in good agreement with available experimental results at the ground state. All these parameters presented the linearly increasing dependences on the external pressure. The B/G ratios and Poisson's ratio indicated that the Al3V and Al3Nb crystals should exhibit brittle behavior at 0–20 GPa. Additionally, the bulk modulus can be obtained through fitting the Birch-Murnaghan equation (B0), computing by VRH method (BH), and deriving from the elastic theory (Brelax) in both intermetallics. The uniformity of these calculated bulk moduli in each compound exhibited the excellent reliability and self-consistency. In addition, Debye temperature was estimated from the average sound velocity. The Debye temperature showed an increasing dependence on the pressures. Finally, through density of states analysis, Al3V and Al3Nb were suggested to possess naturally metallic behavior. Under pressures, it was noted that the shapes of peaks and pseudogaps exhibited relative few changes, suggesting Al3V and Al3Nb has kept structurally stable up to 20 GPa. At zero pressure, Al3Nb was considered as a more structurally stable phase with the more number of bonding electrons per atom than Al3V. This conclusion was in consistent with the one drawn from the thermodynamic analysis.