Temperature Dependence of the Dielectric, Piezoelectric, and Elastic Constants for Pb(Mg1∕3Nb2∕3)O3–PbZrO3–PbTiO3 Piezocrystals

Shujun Zhang,Sung-Min Lee,Dong-Ho Kim,Ho-Yong Lee,Thomas R. Shrout

DOI: https://doi.org/10.1063/1.2817641

IF: 2.877

2007-01-01

Journal of Applied Physics

Abstract:Pb ( Mg 1 ∕ 3 Nb 2 ∕ 3 ) O 3 – Pb Zr O 3 – Pb Ti O 3 (PMN-PZT) ferroelectric single crystals were grown successfully using the solid state crystal growth method. The crystals were found to exhibit higher Curie temperatures TCs and ferroelectric phase transition temperatures TR-Ts when compared to the binary Pb(Mg1∕3Nb2∕3)O3–PbTiO3 system. Specifically the composition 0.4Pb(Mg1∕3Nb2∕3)O3–0.25PbZrO3–0.35PbTiO3 which lies close to the rhombohedral-tetragonal morphotropic phase boundary, was investigated. The full set of materials constants, including elastic (c and s), piezoelectric (d, g, e, and h), and dielectric permittivity (ε∕ε0), were determined using the IEEE standards as a function of temperature ranging between 25 and 100°C. The electromechanical coupling factors k33 and k32 were found to be 93.3% and 93.5%, respectively, with corresponding piezoelectric coefficients d33 and d32 on the order of 1530 and −1440pC∕N. Together with high phase transition temperatures (TC of 216°C and TR-T on the order of 144°C) and high coercive field EC ∼4.6kV∕cm, make PMN-PZT single crystals promising candidates for high temperature actuator and transducer applications.