Microwave Electromagnetic And Absorption Properties Of Nd2fe14b/Alpha-Fe Nanocomposites In The 0.5-18 And 26.5-40 Ghz Ranges

lixian lian,l j deng,min han,waicheung tang,shaodong feng

DOI: https://doi.org/10.1063/1.2712957

IF: 2.877

2007-01-01

Journal of Applied Physics

Abstract:Nd2Fe14B/alpha-Fe nanocomposites were prepared using a melt-spinning method, subsequent annealing treatment, and ball milling. The complex permittivity and permeability of the composites were measured in the 0.5-18 and 26.5-40 GHz frequency ranges. The permeability spectra of the Nd2Fe14B/alpha-Fe nanocomposites exhibit relaxation and resonance type characteristic in the 0.5-18 and 26.5-40 GHz frequency ranges, respectively. The resonance frequency (f(r)) of Nd10Fe78Co5Zr1B6 nanocomposite is 30 GHz due to the large anisotropy field (H-A). However, the resonance frequency of the Nd2Fe14B/alpha-Fe sample is lower than that of Nd2Fe14B, due to the decrease of H-A induced by the exchange interaction between hard and soft magnetic phases. These samples also showed good microwave absorption performance (reflection loss: <-20 dB) in 9, 17, and 35-38 GHz with matching thicknesses of 2, 1.2, and 0.37 mm, respectively. Therefore, Nd2Fe14B/alpha-Fe nanocomposites are thought to be a potential candidate for thinner microwave absorbers not only in the centimeter wave but also in the millimeter wave band. (c) 2007 American Institute of Physics.