Abstract:Solid-state diffusion bonding (DB) of TiAl alloy and Ti2AlNb alloy was carried out using pure Ti as an interlayer at 1000 °C under 20 MPa for 60–120 min. The effects of bonding times on the interfacial microstructure and mechanical performance of the TiAl/Ti/Ti2AlNb bonded joints at room temperature (RT) were investigated detailly. The results demonstrated that the diffusion layers (DLs) mainly consisted of four characteristic layers, (I) single coarse α2 phase adjacent TiAl alloy, (II) single refined α2 phase at the bonding interface, (III) equiaxed/acicular α2 phase embedded in β phase adjacent Ti2AlNb alloy and (IV) both equiaxed α2 phase and acicular O phase embedded in β phase adjacent Ti2AlNb alloy, respectively. The thickness of the four layers increased with the increasing of the bonding time. The growth of DLs is controlled by diffusion and the reaction rate constant k for region I, II, III and IV are 1.22 × 10−6, 1.27 × 10−6, 2.6 × 10−7 and 7.7 × 10−7 m·s−1/2, respectively. Meanwhile, the interface α2 grain grows up without texture. The maximum tensile strength of 281 MPa was maintained at 1000 °C for 90 min under the pressure of 20 MPa. Consequently, the phase transformation and dynamic recrystallization behavior of the DLs were discussed.<h3 class="a-plus-plus">Graphic abstract</h3>

Effects of Electric Field on Interfacial Microstructure and Shear Strength of Diffusion Bonded Α-Al2o3/ti Joints

Interface Behaviors and Mechanical Properties of Diffusion Bonded 45 Steel/additive Manufactured 316L Steel Joints

Structure and forming process of the Ti/Al diffusion bonding joints

Formation Process of the Bonding Joint in Ti/Al Diffusion Bonding

Interface Evolution Behaviors and Shear Strength of Vacuum Diffusion Bonded 45 Steel/additive Manufactured 316L Stainless Steel Joints

Diffusion Interface Evolution of Low-Alloy Steel Q235 and Ti by Electro-Assisted Hot-Pressing Bond

Interface characteristic and mechanical performance of TiAl/Ti2AlNb diffusion bonding joint with pure Ti interlayer

Ceramic Bonding and Joint'S Strengthening Through Forming Intermetallic Compounds in Situ

The influence of electrical/thermal fields on the microstructure and mechanical properties of Ti2AlNb alloy from the view of molecular dynamics

Effects of doping Ti3SiC2 with Al on interfacial microstructural evolution, growth kinetics and mechanical properties of Ti3SiC2/TiAl joints

Evaluation of electrically-assisted vacuum diffusion bonding of a TiBw/TA15 composite by microstructural analysis and mechanical testing

Investigation on the Diffusion Behaviors and Mechanical Properties of the Ti/Al Interface Using Molecular Dynamics Simulation

Vacuum diffusion bonding of Ti2AlNb alloy and TC4 alloy

Bonding Ceramics with Al/Ti/Al Multilayers by in Situ Formation of Intermetallic Compound

A novel high entropy composite interlayer for diffusion bonding of TC4 titanium alloy to 316 L stainless steel

Interfacial microstructure and mechanical properties of diffusion bonded joints of additive manufactured 17-4 PH stainless steel and TC4 titanium alloy

Interface evolution mechanism and mechanical properties of Ti311/TC4 laminated composites during hot-pressing diffusion bonding

Bonding pressure effects on characteristics of microstructure, mechanical properties, and mass diffusivity of Ti-6Al-4V and TiAlNb diffusion-bonded joints

Diffusion bonding of implantable Al2O3/Ti-13Nb-13Zr joints: Interfacial microstructure and mechanical properties

Structure and Performance of LF6/TA2 Diffusion Bonded Joint

Spark Plasma Diffusion Bonding of TiAl/Ti2AlNb with Ti as Interlayer