Cd1−xBix(Cd1+xIn1−x)VO6 (0 ≤ X ≤ 0.14): A New Polar Oxide with Second-Harmonic Generation

Tao Yang,Junliang Sun,Jeongho Yeon,P. Shiv Halasyamani,Shiliang Huang,Joachim Hemberger,Martha Greenblatt

DOI: https://doi.org/10.1021/cm101582j

IF: 10.508

2010-01-01

Chemistry of Materials

Abstract:The structure of the new polar oxide, Cd2InVO6, was determined by powder X-ray diffraction. Cd2InVO6 crystallizes in space group P3(1) with the unit cell parameters: a = 12.21896(4), c = 9.256 75(4) angstrom. The Cd2+ and In3+ ions are statistically disordered in nine independent positions (M1-M9) with a certain level of site preference. M1-M3 form highly asymmetric oxygen-coordination polyhedra, which are similar to those formed by alkali or alkali-earth cations. M4-M9 are in distorted octahedral cavities. It is shown that M1-M3 are likely occupied mostly by Cd2+ while M4-M9 are extensively mixed by Cd2+ and In3+. The structure is best described as a framework of interconnected M4-M9 distorted octahedra with the M1-M3 polyhedra off-framework and the three independent VO4 tetrahedra filling the channels of the framework structure by corner-sharing with the MO6 octahedra. The polar framework is composed of M4O(6)similar to M9O(6) octahedra in a five-connected net with the topology nomination (3(3), 6(3), 9(4)), The Bi3+-substituted compounds were also investigated with the rationale that the lone pair electrons of Bi3+ might enhance ferroelectricity. Single phase Cd1-xBix(Cd1+xIn1-x)VO6 forms limited solid solutions (0.02 <= x <= 0.14). Ferroelectricity was observed for neither the parent nor the Bi3+-substituted compounds, which suggest that the dipole moments are not switchable or too insignificant in magnitude. The powder second-harmonic generation measurements with 1064 nm radiation established that Cd1-xBix(Cd1+xIn1-x)VO6 are type-1 phase-matchable materials for x = 0, 0.14 with 70 and 90 times the efficiency of alpha-SiO2, respectively.