Process of degumming by chemical for banana pseudostem fibers and characterization of degummed fibers
Xu Shuying,Tan Wei,Zhang Yucang
DOI: https://doi.org/10.11975/j.issn.1002-6819.2015.13.042
2015-01-01
Abstract:Natural fibers have growing demands in textile industry due to its availability, eco-friendliness, renewability, CO2-neutrality, flexibility, low density and low cost. Banana pseudostem fibers (BPSFs) can be a potential candidate to replace the synthetic fibers. However, there are still limitations for their application in textile industry because of their poor quality, such as “coarseness, shortness, hardness and crispness”. This paper described one chemical method for extracting finer natural BPSFs from natural banana pseudostem. The effects of different pre-acid, pre-oxygen and alkali cooking processes on degumming rate and residual lignin rate of BPSFs were studied. The better degumming process was determined. The physicochemical properties of BPSFs treated chemically were analyzed by using the Fourier transformed infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). FTIR revealed structural modification after chemical treatments. SEM was used to evaluate the fracture morphology of failed samples. The tensile properties of BPSFs treated chemically were also investigated. The result showed that the pre-acid process condition was 2 g/L H2SO4 aqueous solution at 55 °C for 2 h, where the external wax could be removed. The pre-oxygen process was achieved by immersing the banana pseudostem in a 200 mL mixture liquid composed of 7 g/L H2O2, 3wt% Na2SiO3 and 2wt% sodium polyphosphate at 95 °C for 1.5 h. Afterwards, The sample was immersed in 200 mL NaOH solution of 9 g/L at boiling temperature for 3 h, then washed with 1 g/L H2SO4 for 2-3 min to neutralize the residual alkali in the sample. Under the conditions, the residual gum rate of BPSFs treated chemically was 20.80%, and the residual lignin rate was 8.21%. BPSFs treated chemically were white and clean, and consisted of a large number of fine micro fibrils with a diameter of from 0.05 to 0.09 mm. In addition, BPSFs treated chemically were soft. FTIR results showed that most of the hemicelluloses and lignin were removed by chemical treatments, and the relative crystallinity index of BPSFs treated chemically was 61.2%. The SEM of longitudinal morphologies of BPSFs treated chemically had a cleaner, rougher, and fibrillated fiber surface due to dissolution of hemicelluloses and lignin. The SEM diagram indicated the BPSFs treated chemically exhibited a combination of ductile and brittle failure. Tensile test was carried out on single fiber according to the ASTM D 3822-01 standard. The diameter of BPSFs treated chemically was within the range of 0.068 mm, and the tensile strength, Young’s modulus and elongation rate were 353.09 MPa, 18.34 GPa and 1.70% respectively. The tensile strength and elongation rate were enhanced by 13% and 6.5% respectively in the BPSFs treated chemically compared to those of untreated ones. And the Young’s modulus was decreased by 14% in the BPSFs treated chemically compared to those of untreated ones. The tensile properties of BPSFs treated chemically were correlated with the results of FTIR, XRD and SEM. Based on the properties of BPSFs treated chemically, we expect that these fibers will be suitable for the use as textile materials.