Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Cyclic Behavior of 9–12% Cr Steel under Different Control Modes in Low Cycle Regime: A Comparative Study

Cyclic Softening Behaviors of Modified 9–12%cr Steel under Different Loading Modes: Role of Loading Levels

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Low Cycle Fatigue of 9-12% Cr Steel at Elevated Temperature: Cyclic Deformation Behavior and Life Assessment

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

The cyclic response behavior, failure mechanism, and life prediction model of 9% Cr‐based steel under different strain ratios in the low cyclic fatigue regime at 430°C

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Interaction of Cyclic Softening and Stress Relaxation of 9–12% Cr Steel under Strain-Controlled Fatigue-Creep Condition: Experimental and Modeling

Modeling of Low Cycle Behavior of P92 Steel Based on Cyclic Plasticity Constitutive Equations

Effect of Cyclic Loadings on Stress Relaxation Behaviors of 9–12%cr Steel at High Temperature

Uniaxial Mean Stress Relaxation of 9–12% Cr Steel at High Temperature: Experiments and Viscoplastic Constitutive Modeling

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Creep-fatigue interaction and damage behavior in 9-12%Cr steel under stress-controlled cycling at elevated temperature: Effects of holding time and loading rate

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Simulation of Cyclic Deformation Behavior of Ferritic P92 Steel Based on Unified Viscoplastic Model

Cyclic deformation and damage mechanisms of 9%Cr steel under hybrid stress-strain controlled creep fatigue interaction loadings

Cyclic stress response and microcrack initiation mechanism of modified 9Cr‐1Mo steel under low cycle fatigue at room temperature and 350°C

A comparative study of low cycle fatigue behavior and microstructure of Cr-based steel at room and high temperatures