Size-Dependent Multiple Magnetic Phases and Exchange Bias Effect in Hole-Doped Double Perovskite La1.6sr0.4nimno6

Wenjie Liu,Lei Shi,Shiming Zhou,Jiyin Zhao,Yang Li,Yuqiao Guo

DOI: https://doi.org/10.1088/0022-3727/47/48/485003

2014-01-01

Abstract:La1.6Sr0.4NiMnO6 nanoparticles of different sizes (18-150 nm) have been prepared by a sol-gel method, and the size effects on their magnetic properties are investigated. It is found that there is a ferromagnetic (FM) transition at T-C similar to 245 K for the sample with particle size D similar to 150 nm. As the particle size decreases, a spin glass (SG) transition appears at T-G similar to 60 K and becomes more obvious. Meanwhile, the T-C shifts to a lower temperature and the FM transition becomes indistinct. The size dependent saturation magnetization M-S, which is in the range 0.78 similar to 1.27 mu(B)/f.u., shows a non-monotonic variation with a maximum of 1.27 mu(B)/f.u. at the particle size D-C similar to 42 nm. The exchange bias (EB) effect is clearly observed for D > 32 nm and becomes indistinct as D <= 32 nm. As the particle size decreasing, the EB field H-E decreases and becomes near nil at D-C. Meanwhile, the coercive field H-C first increases to a maximum at D-C and then decreases. All the results indicate the coexistence of AFM APBs related to the anti-site disorders, FM domains, and SG phase in La1.6Sr0.4NiMnO6 nanoparticles. The magnetic properties of the nanoparticles are understood by a complex core-shell model, i.e. both AFM APBs and FM domains coexist in the core, and the SG phase mainly resides on the surface (shell) of each particle, which reveals that the size effects on the FM phase, AFM APBs and surface SG phase in grain are different, even are opposite. The nanometer size effect is a crucial factor to influence the magnetic properties of La1.6Sr0.4NiMnO6 nanoparticles.