Photocatalysts Based on Graphitic Carbon Nitride: Some Prospects for Artificial Photosynthesis and the Remediation of Environmental Pollution
C. Rhodes
DOI: https://doi.org/10.3184/003685017X15063357842592
2017-11-01
Abstract:Graphitic carbon nitride (g-C3N4) is a polymeric semiconductor which may offer considerable promise as a photocatalyst, in consideration of its band structure with an appreciable absorption of light in the visible region (which comprises 43% of the solar spectrum), high physicochemical robustness, and that it can be readily synthesised from earth-abundant materials1. Thus, it may be prepared from such relatively common nitrogen-rich organic starting materials as melamine, urea, cyanamide, dicyananamide, thiourea and ammonium thiocyanate. The structure is based on heptazine (also called tri-s-triazine or cyamelurine) units (Figure 1), which possess a planar triangular core group, C6N7, or three fused triazine rings, with three substituents at the corners of the triangle. (The development2 of the g-C3N4 structure by heating melamine, as a starting material, is shown in Figure 2.) Carbon nitride polymers have a long history, in fact, which extends back to the 1830s, when Jöns Jakob Berzelius discovered a polymeric substance formed by the ignition of mercury thiocyanate, which was later named melon, by Justus von Liebig3. Melon is a linear polymer of heptazine units linked together by secondary amino groups (Figure 2). It was in 2006 that interest in g-C3N4 as a metal-free photocatalyst began 4, which was first explored5 for H2 production in 2009. Among the seven known phases of C3N4, g-C3N4 is the most stable, and has the lowest band gap at 2.7–2.8 eV. This corresponds to a light absorption range of 450–460 nm, which brings it into the visible region, in contrast with TiO2, with a band gap of around 3.2 eV (400 nm), meaning that it only absorbs UV radiation (although many ingenious structural modifications have been attempted in order to coerce the essential material to absorb visible light). There are, nonetheless, various deficiencies1 presented by g-C3N4, which include a rapid rate of recombination of charge carriers (electrons and holes), unsatisfactory electrical conductivity, and that the unmodified material does not absorb light at wavelengths longer than 460 nm. However, it has been found that co-polymerisation and doping
Chemistry,Biology,Environmental Science,Medicine