High density Fe-based soft magnetic composites with nice magnetic properties prepared by warm compaction
Haohui Huang,Rui Zhang,Haibo Sun,Jichao Zhang,Jinghui Wang
DOI: https://doi.org/10.1016/j.jallcom.2023.169460
IF: 6.2
2023-03-08
Journal of Alloys and Compounds
Abstract:The influences of compacting temperature ( T c ), molding pressure ( P m ), contents of lubricant ( C l ) and binder ( C b ) on the compacted density ( ρ c ) and its comprehensive soft magnetic properties for the FeSiCr soft magnetic composites (SMCs) fabricated by warm compaction were systematically studied. Appropriate increase of T c is beneficial to improve the surface lubrication effect of magnetic powders during the forming process of SMCs, thus giving rise to the increase of ρ c and the decrease of porosity fraction for the SMCs. Under this situation, the resistance of domain rotation and domain wall displacement in the SMCs during magnetization process is reduced, which is finally in favor of the improvement of SMCs's soft magnetic properties. The results of loss separation show that the P h value plays a dominant role in the variation trend of P cv value for the FeSiCr-SMCs in the test frequency range of 20–200 KHz, wherein the ratio of P h / P cv is large than 81 %. Under the optimized process parameters of T c = 110 °C, P m = 600 MPa, C l = 1.5 wt. % and C b = 2.5 wt. %, the ρ c of FeSiCr-SMCs increases by 8.14 % to 6.38 kg/m 3 , and the SMCs exhibit better comprehensive soft magnetic properties compared with those at T c = 25 °C. Hereinto, μ e increases by 19.89 % to 45.8 @ 100 kHz, P cv decreases by 26.11 % to 495.8 kW/m 3 @ f = 100 kHz, B m = 50mT, and μ e % reached 85.5 % at H = 8000 A/m. These results indicated that the warm compaction process is one of the effective ways to further promote Fe-based SMCs to meet the development requirements of high-frequency, miniaturization and high-power of electronic equipment.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering