Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy
Qingqing Ding,Hongbin Bei,Xia Yao,Xinbao Zhao,Xiao Wei,Jin Wang,Ze Zhang
DOI: https://doi.org/10.1016/j.apmt.2021.101061
IF: 8.663
2021-01-01
Applied Materials Today
Abstract:Mechanical behaviors of a Ni-based single crystal superalloy have been investigated by tensile testing at various temperatures. Deformation substructures and mechanisms have been systemically revealed from micrometer to atomic scales by using advanced scanning electron and scanning transmission electron microscopes. Results show that deformation mode of the alloy strongly depends on the temperature due to competitive responses of the gamma and gamma' phases under mechanical loading and their original stress statuses. At temperatures from ambient to 750 degrees C, plasticity is governed by dislocation shearing in both phases, where slip modes of gamma are < 110 >{111} and those of gamma' are < 112 >{111}, < 110 >{111} and < 110 > {001}. At moderate temperatures (850 degrees C <= T <= 900 degrees C), plasticity mainly involves microscopically uniform deformation of both phases. The matrix deforms first so that channels parallel to tensile direction are narrowed due to the Poisson's effect, after that deformation of gamma' follows. The active slip modes are < 110 > {111} for gamma, < 112 >{111}, < 110 >{111}, < 110 >{001}, and < 001 >{001} for gamma'. At temperature higher than 1000 degrees C, plastic strain is also derived from deformation of both phases, but deformation of the matrix plays critical roles, due to relatively weak strength of this phase. The operative slip modes are < 110 > {111} for gamma, but mainly < 110 >{001} and < 001 >{001} for gamma'. Our results clearly provide a comprehensive and multiscale (from micrometer to atomic) understanding on the deformation mechanism of Ni-based superalloys, which can be critically beneficial and offer mechanistic guidelines to design new/next generation superalloys. (c) 2021 Elsevier Ltd. All rights reserved.