Abstract:3D NiχCo1−χ oxides with different morphologies for high-capacity supercapacitors were controllably synthesized via an electrodeposition method combined with a simple post annealing process. The synthesis involves the co-electrodeposition of the bimetallic (Ni, Co) hydroxide precursor on a nickel foam scaffold and subsequent thermal transformation to NiχCo1−χ oxides. The crystalline structure, morphology and electrochemical performance of the 3D NiχCo1−χ oxides can be readily manipulated by simply varying the Co/Ni molar ratio in the electrodeposition electrolyte. With the increase of the Co/Ni molar ratio, the characteristic peak intensities and the signal sites were gradually changed from a NiO crystal dominant structure to NiCo2O4 and finally to a Co3O4 dominant structure. Moreover, the morphology also can be controlled by adjusting the Co/Ni molar ratio in the electrodeposition electrolyte. In addition, the Ni0.61Co0.39 oxide electrode shows a large specific capacitance of 1523.0 F g−1 at 2 A g−1 and 95.30% of that can be retained, even at a high current density of 30 A g−1. The superior rate capability should be attributed to the unique 3D network-like architecture, which can enlarge the liquid–solid interfacial area, facilitate the electron and ion transport, and further increase the utilization of the active material. To demonstrate its practical application, an asymmetric supercapacitor based on the Ni0.61Co0.39 oxide electrode as a positive electrode and activated carbon as a negative electrode was fabricated. Owing to the outstanding capacitive behavior of the Ni0.61Co0.39 oxide electrode, the asymmetric device delivers a prominent energy density of 36.46 W h kg−1 at a power density of 142 W kg−1, and which holds great promise for potential applications in energy storage.

Cu-Doped Nio for Aqueous Asymmetric Electrochemical Capacitors

Efficient Utilization of Oxygen-Vacancies-enabled NiCo2O4 Electrode for High-Performance Asymmetric Supercapacitor

Engineering of Co3O4 electrode via Ni and Cu-doping for supercapacitor application

Characterization of NiCo2 O4 as high-performance supercapacitor electrode materials

Ammonia-induced N-doped NiCoO2 Nanosheet Array on Ni Foam As a Cathode of Supercapacitor with Excellent Rate Performance

Ultrathin Mesoporous Nio Nanosheet-Anchored 3d Nickel Foam As An Advanced Electrode For Supercapacitors

Nanospherical Cu2O/NiO Synthesized by Electrochemical Dealloying As Efficient Electrode Materials for Supercapacitors

Nickel-Copper Bimetallic Oxide Nanoparticles Prepared by Simple Coprecipitation Method as High Performance Electrode Materials for Asymmetric Supercapacitors

One-pot synthesis of Cu-doped Ni3S2 nano-sheet/rod nanoarray for high performance supercapacitors

Modulation of p‐ and n‐Type Transitions in Co3−xNixO4 Nanoparticles for Enhanced Supercapacitor Electrochemical Performance

Facile Synthesis of Al-doped NiO Nanosheet Arrays for High-Performance Supercapacitors

Design and synthesis of nitrogen-doped hexagonal NiCoO nanoplates derived from Ni-Co-MOF for high-performance electrochemical energy storage

Synthesis and Characterization of Nickel-doped Manganese Dioxide Electrode Materials for Supercapacitors

Tuning the Crystal Structure of NiS/carbon by Mo Doping for Asymmetric Supercapacitor Application

Distinctive Supercapacitive Properties of Copper and Copper Oxide Nanocrystals Sharing a Similar Colloidal Synthetic Route

Synthesis and capacitance performances of Ni–Mn-Oxides as electrode materials for high-performance supercapacitors

Application of Chemical Doping and Architectural Design Principles To Fabricate Nanowire Co2Ni3ZnO8 Arrays for Aqueous Asymmetric Supercapacitors.

Oxygen-doped NiCoP derived from Ni-MOFs for high performance asymmetric supercapacitor

Controllable synthesis of 3D NiχCo1−χ oxides with different morphologies for high-capacity supercapacitors

3D Hierarchical Urchin-Like Ni 0.3 Co 0.6 Cu 0.1 (CO 3 ) 0.5 (OH) Microspheres for Supercapacitors with High Specific Capacitance

Supercapacitor performance of pure and Ni-doped CuO electrodes prepared by USP