Abstract:Nanostructured mesoporous manganese oxides were easily prepared by mixing KMnO4 with ascorbic acid in an aqueous solution under ambient conditions. The obtained manganese oxides were identified as having an alpha-MnO2 tunnel structure composed of an edge-shared network of [MnO6] octahedra. TEM observations revealed that the obtained MnO2 materials had three-dimensional frameworks which consisted of homogeneous nanoparticles with sizes of ca. 5 nm. Nitrogen sorption analyses showed that these MnO2 nanoparticles exhibited a type IV isotherm, indicating a mesoporous character. Large surface areas up to 284 m(2) g(-1) were recorded. The electrochemical performances of the synthesized alpha-MnO2 nanoparticles as supercapacitor electrode materials were studied using cyclic voltammetry and galvanostatic charge-discharge cycling in a three-electrode system at a potential range from 0 to 1.0 V vs a saturated calomel electrode in 0.5 M sodium sulfate solution. The result showed that mesoporous MnO2 with three-dimensional frameworks exhibit a high capacitance up to similar to 200 F g(-1). Furthermore, a hybrid supercapacitor was assembled by using MnO2 mixed with a small amount of activated carbon as the positive electrode and activated carbon as the negative electrode in a 0.5 M Na2SO4 electrolyte. By balancing the mass of MnO2 and activated carbon, a practical cell voltage of 1.8 V could be obtained in aqueous medium with a capacitance of 23.1 F g(-1). After 1200 cycles, the maximum energy density is 104 Wh kg(-1) and power density is 14.7 kW kg(-1). Thus, the obtained alpha-MnO2 nanoparticles are suitable for use as supercapacitor electrode materials.

Rational Design of Manganese Dioxide Decorated Skeleton of Colloidal Mesoporous Carbon Nanocomposites for Supercapacitors

Development Of Mno2/Porous Carbon Microspheres With A Partially Graphitic Structure For High Performance Supercapacitor Electrodes

Manganese Doped Co3O4 Mesoporous Nanoneedle Array for Long Cycle-Stable Supercapacitors

Supramolecule-assisted Synthesis of In-Situ Carbon-Coated MnO2 Nanosphere for Supercapacitors

Engineering Nanostructured Mno2 For High Performance Supercapacitors

Novel Mesoporous Carbon-Carbonaceous Materials Nanostructures Decorated with Mno2 Nanosheets for Supercapacitors

Hierarchical Manganese Oxide/Carbon Nanocomposites for Supercapacitor Electrodes

Three-Dimensional (3d) Nanocomposites of Mno2-Modified Mesoporous Carbon Filled with Carbon Spheres/Carbon Blacks for Supercapacitors

Preparation and Electrochemical Properties of Mesoporous Manganese Dioxide-Based Composite Electrode for Supercapacitor

Manganese Dioxide-Coated Activated Mesocarbon Microbeads for Supercapacitors in Organic Electrolyte

MnO2 Nanoflakes/hierarchical Porous Carbon Nanocomposites for High-Performance Supercapacitor Electrodes

In-situ Synthesis of MnO2@Graphdiyne Oxides Nanocomposite with Enhanced Performance of Supercapacitors

Facile Fabrication of Mesoporous Manganese Oxides As Advanced Electrode Materials for Supercapacitors

Carbon Cloth@t-Nb2o5@mno2: A Rational Exploration of Manganese Oxide for High Performance Supercapacitor

Synthesis of Nanostructured Mesoporous Manganese Oxides with Three-Dimensional Frameworks and Their Application in Supercapacitors

Nanoarchitectured MnO2 Confined to Mesoporous Carbon Microspheres As Bifunctional Electrodes for High-Performance Supercapacitors and Lithium-Ion Capacitors

A new strategy for synthesis of hierarchical MnO2–Mn3O4 nanocomposite via reduction-induced exfoliation of MnO2 nanowires and its application in high-performance asymmetric supercapacitor

Carbon spheres-assisted strategy to prepare mesoporous manganese dioxide for supercapacitor applications

Morphology-Controlled Mno2-Graphene Oxide-Diatomaceous Earth 3-Dimensional (3d) Composites for High-Performance Supercapacitors

Nanostructured Manganese Dioxide with Adjustable Mn3+/Mn4+ Ratio for Flexible High-Energy Quasi-Solid Supercapacitors

Facile Synthesis of Mn3O4 Nanoparticles Decorated Graphene as Enhanced Performance Electrode for Supercapacitor