Abstract:Ti(C,N)-xCrMnFeCoNi-(15wt.%-x)Ni cermets (x = 0wt.%, 5wt.%, 10wt.%, 15wt.%) were fabricated by low-pressure sintering. Because of the sluggish diffusion effect of high-entropy alloy (HEA), the grain growth of cermets containing HEA binder is inhibited. The FCC binder phases of cermets with CrMnFeCoNi/Ni binders generate a uniform dispersion, motivating to form many complete and moderate rim phases and wet the ceramic particles. Furthermore, the hardness of cermets roughly increases, while the strength and fracture toughness maintain the change tendency of rising the peak and then falling with CrMnFeCoNi additions. Ti(C,N)-5wt.% CrMnFeCoNi-10wt.% Ni cermets obtains a prominent mechanical property combination with hardness of 1646 ± 13.5 HV30, strength of 2181 ± 167.2 MPa and fracture toughness of 9.1 ± 0.11 MPa m1/2. Besides, the cermets containing CrMnFeCoNi/Ni binders obtain reduced friction coefficients and low wear rates at 750 °C compared with Ti(C,N)–Ni cermets and Ti(C,N)-HEA cermets. The superior high-temperature wear resistance is ascribed to the thermal softening resistance of CrMnFeCoNi, strengthening and toughening effect of CrMnFeCoNi/Ni on matrix and the transition of wear mechanism from abrasive wear and the removal of tribochemical layers to the removal of tribochemical layers. The cutting lifetime of cermets containing CrMnFeCoNi/Ni binders is increased by 40%–70% in comparison with Ti(C,N)–Ni cermets during machining 17-4 PH stainless steel. Concisely, Ti(C,N)-based cermets with outstanding mechanical, wear resistance and cutting properties can be obtained by partially replacing Ni with 5–10 wt.% CrMnFeCoNi.

Effect of WC content on microstructure and mechanical properties of Ni3Al-bonded cermets

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Effects of WC content on core/rim phases and microstructure of TiB2-TiC-WC-(Co-Ni) cermets

Effect of Ni content on the microstructure and properties of WCoB-TiC cermets

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effect of WC-Co Granules on Mechanical Properties and Microstructure of Ti(C,N)-based Cermets

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Effect of WC Content on Thermal Shock Resistance of Ti(C,N)-based Cermets

Macro/microstructure Evolution and Mechanical Properties of Ti33.3Al Alloys by Adding WC Particles

Influence of C and Al Addition on Microstructure and Mechanical Properties of Ultrafine TiCN-Based Cermets

Effect of Mo Addition on Microstructure, Magnetic and Mechanical Properties of TiC-TiN-WC-Ni Cermets

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Effects of WC/TiC addition on the thermodynamic behavior of TiB 2 -based cermet during sintering process

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides