Abstract:Mesoporous solid strong bases are highly promising for applications as environmentally benign catalysts in various reactions. Their preparation attracts increasing attention for the demand of sustainable chemistry. In the present study, a new strategy was designed to fabricate strong basicity on mesoporous silica by using multifunction of a carbon interlayer. A typical mesoporous silica, SBA-15, was precoated with a layer of carbon prior to the introduction of base precursor LiNO3. The carbon interlayer performs two functions by promoting the conversion of LiNO3 at low temperatures and by improving the alkali-resistant ability of siliceous host. Only a tiny amount of LiNO3 was decomposed on pristine SBA-15 at 400 °C; for the samples containing >8 wt % of carbon, however, LiNO3 can be entirely converted to strongly basic sites Li2O under the same conditions. The guest-host redox reaction was proven to be the answer for the conversion of LiNO3, which breaks the tradition of thermally induced decomposition. More importantly, the residual carbon layer can prevent the siliceous frameworks from corroding by the newly formed strongly basic species, which is different from the complete destruction of mesostructure in the absence of carbon. Therefore, materials possessing both ordered mesostructure and strong basicity were successfully fabricated, which is extremely desirable for catalysis and impossible to realize by conventional methods. We also demonstrated that the resultant mesoporous basic materials are active in heterogeneous synthesis of dimethyl carbonate (DMC) and the yield of DMC can reach 32.4%, which is apparently higher than that over the catalysts without a carbon interlayer (<12.9%) despite the same lithium content. The strong basicity, in combination with the uniform mesopores, is believed to be responsible for such a high activity.

One-Pot Synthesis of Zeolitic Strong Solid Bases: A Family of Alkaline-Earth Metal-Containing Silicalite-1

Mg2+-derived mesoporous ultra-high silica twelve-membered-ring basic zeolites: straightforward synthesis and catalytic performance

Novel solid strong base derived from zeolite supported CaO*

Amine-free synthesis of high-silica MFI zeolite by the conventional hydrothermal route

Frontispiece: Co‐hydrolysis and Seed‐Induced Synthesis of Basic Mesoporous ZSM‐5 Zeolites with Enhanced Catalytic Performance

Controllable and SDA-free synthesis of sub-micrometer sized zeolite ZSM-5. Part 1: Influence of alkalinity on the structural, particulate and chemical properties of the products

Alcohol-assisted synthesis of high-silica zeolites in the absence of organic structure-directing agents

Conventional Hydrothermal Synthesis of MFI Zeolite in Methanol Solution

One-pot synthesis of silanol-free nanosized MFI zeolite

Generalized Ionothermal Synthesis of Silica-Based Zeolites

Imidazolium salts facilitate mechanochemical synthesis of well-dispersed MFI zeolite crystals with c-axis orientation

Base property of high silica MFI zeolites modified with various alkyl amines

The strong SDA/framework interactions and acidity study of high-silica LTA-type zeolites

Synthesis of b-axis oriented high silica MFI type zeolite crystals introduced with co-template role

Preparation and Structural Characterization on Organic-inorganic Hybrid Acid-base Bifunctional High Silica Y Zeolite

Alkaline synthesis of pure silica ITH zeolite for vapor phase Beckmann rearrangement of cyclohexanone oxime

Low-temperature fabrication of mesoporous solid strong bases by using multifunction of a carbon interlayer

Synthesis and Structure Analysis of Zeolite AS-1 from HF–Al2O3–SiO2–ethylenediamine–H2O

One‐pot Synthesis of Binderless Zeolite A Spheres Via in Situ Hydrothermal Conversion of Silica Gel Precursors

Attempt to Generate Strong Basicity on Silica and Titania