Abstract:We synthesized a self-healing polyurethane elastomer (PU-SSDA) which displayed excellent healing efficiency at room temperature due to the synergistic contribution of dynamic covalent D-A bond and S-S bond. Mechanical and self-healing properties of the polyurethane elastomers were characterized by tensile test and three-dimensional super depth of field microscope. The cross-linking structure of PU-SSDA is explored by extraction experiments, demonstrating that there are not only crosslinked structures but also linear molecular segments existed in the polyurethane elastomer. Mechanical properties of the PU-SSDA elastomer can be tuned by changing the cross-linking degree. As the crosslinking degree increases from 25% to 45%, the tensile strength increases from 2.9 MPa to 5.5 MPa while the elongation at break decreases from 795% to 304%. After optimization, when the crosslinking degree was 35%, the tensile strength was 3.7 MPa, the elongation at break was 606% and the repair efficiency could be restored to 93% after healing for 60 min at room temperature. Moreover, the healing efficiency still remains above 90% after 4 damage-healing cycles. In addition, the PU-SSDA elastomer can also be reprocessed by hot pressing at 120 degrees C. This excellent self-healing behavior and reprocessable property were attributed to the reversible fracture recombination reaction of dynamic D-A and S-S bonds and the quick infiltration of the linear polymer chains into damaged surface. The self-healing mechanism can be further confirmed by the dissolution experiments which showed that the PU-SSDA elastomer can be dissolved in DMF at 100 degrees C while the PU-control can only swell under the same conditions, demonstrating that the reversible cleavage and reformation of D-A and S-S bonds contribute a lot to the self-healing process. Due to the facile and friendly preparation method, fast self-healing behavior at room temperature and fully reprocessable properties, the as prepared polyurethane elastomers displayed wide potential applications such as protection coatings and wearable electronic devices.

Self-healing Polyurethane Elastomer with Thermally Reversible Alkoxyamines As Crosslinkages

Self-Healing Polyurethane-Urea Elastomers with High Strength and Toughness Based on Dynamic Hindered Urea Bonds and Hydrogen Bonds

A Tough Polyurethane Elastomer with Self-Healing Ability

Recyclable Self-Healing Polyurethane Cross-Linked by Alkyl Diselenide with Enhanced Mechanical Properties

Alkoxyamine with Reduced Homolysis Temperature and Its Application in Repeated Autonomous Self-Healing of Stiff Polymers

Preparation And Characterization Of Thermally Reversible Self-Healing Polyurethane Elastomer

Room-temperature Self-healable and Reprocessable Polyurethane Elastomers Combined Diels-Alder Bond and Disulfide Bond

Self-Healing Polyurethane Elastomers with High Mechanical Properties Based on Synergistically Thermo-Reversible and Quadruple Hydrogen Bonds

Robust, Transparent, and Self-Healable Polyurethane Elastomer Via Dynamic Crosslinking of Phenol-Carbamate Bonds

UV‐curable Polyurethane Elastomer with UV‐irradiation/Thermo Dual‐Activated Self‐healability

A combined experimental and molecular dynamics simulation study of an intrinsic self-healing polyurethane elastomer based on a dynamic non-covalent mechanism

Research on Self-healing Polypolyurethane Elastomer Based on Multiple Reversible Action

Polyurethane-based crosslinked polymer with tunable self-healable and mechanical properties

Self-healing and reprocess of crosslinked polyurethane based on dynamic oxime-carbamate bond

Self-healing Polyurethane Elastomer Based on Molecular Design: Combination of Reversible Hydrogen Bonds and High Segment Mobility

Designing an elastomeric polyurethane coating with enhanced mechanical and self-healing properties: The influence of disulfide chain extender

Synthesis and Characterization of Linear Self-Healing Polyurethane Based on Thermally Reversible Diels–Alder Reaction

Room Temperature Self-Healable Epoxy Elastomer with Reversible Alkoxyamines As Crosslinkages

Design and Development of Self‐repairable and Recyclable Crosslinked Poly(thiourethane‐urethane) Via Enhanced Aliphatic Disulfide Chemistry

Polybutadiene Derived Allophanate As the Crosslinker for Diels–Alder Type Self‐healing Polyurethane Networks

Polyether–maleimide‐based Crosslinked Self‐healing Polyurethane with Diels–Alder Bonds