Lead-free electrostrictive (Bi 0.5 Na 0.5 )TiO 3 –(Bi 0.5 K 0.5 )TiO 3 –(K 0.5 Na 0.5 )NbO 3 ceramics with good thermostability and fatigue-free behavior

Jigong Hao,Zhijun Xu,Ruiqing Chu,Wei Li,Juan Du

DOI: https://doi.org/10.1007/s10853-015-9080-3

IF: 4.5

2015-01-01

Journal of Materials Science

Abstract:In this study, we designed a series of compositions deep in pseudocubic region based on ternary (1− x )[(1− y )(Bi 0.5 Na 0.5 )TiO 3 – y (Bi 0.5 K 0.5 )TiO 3 ]– x (K 0.5 Na 0.5 )NbO 3 (BNKT100 y –100 x KNN) system for electrostrictive applications. Results show that the KNN substitution into BNKT100 y induces a significant disruption of the ferroelectric order, and tends to enhance the electrostrictive properties of the ceramics. A high, purely electrostrictive effect with large electrostrictive coefficient Q 33 of 0.025 m 4 /C 2 and good thermostability comparable with that of traditional Pb-based electrostrictors is obtained for BNKT100 y – x KNN ( y = 0.20, x = 0.16) ceramics, which lies deep in pseudocubic region along the MPB compositions of the ternary system. Temperature-dependent structural analysis suggests that the good electrostrictive properties insensitive to temperature can be ascribed to the stable relaxor pseudocubic phase over a wide temperature range. Furthermore, it is found that the electrostrictive coefficient Q 33 exhibits only small degradation within 2 % at the field amplitude of 80 kV/cm up to 10 5 switching cycles. The large and purely electrostrictive effect with the exceptionally good fatigue resistance and thermostability makes this material a great potential to be applied to the environmental-friendly solid-state actuators.