Abstract:A kind of hydrophobic silica with good dispersibility was prepared first. The silica and epoxy natural rubber (ENR) were blended in Haake internal mixer at high temperature in a powerful shear force filed, and so the grafted silica was made through in-situ grafting reaction between the hydroxyl groups of silica and the epoxy groups of ENR. The grafting processes were performed as follows: first, the silica should be dried about 24 h at 100 degrees C in an oven to remove the free water molecules that absorbed on the surface of silica. Secondly, the grafting reaction temperature was chosen at 170 degrees C that confirmed by the test result of a Monsanto MDR-2000 moving die rheometer, and the weight proportions between silica and ENR were chosen to be 1: 1, 2: 1 and 3: 1 separately in this study. Thirdly, ENR was mixed in HAAKE internal mixer about I min, then silica was added to react with the ENR for another 15 min before discharged, and the outputs named ENR-grafted silica were obtained as we wanted. In order to obtain an appropriate grafting condition, the effect of different weight proportions between silica and ENR on the stress-strain curves of natural rubber composites reinforced by the grafted silica was discussed. Through analyses of the reinforcement effect, the appropriate proportion between silica and ENR was chosen to be 3: 1. FTIR, TGA and TEM analysis results indicated that ENR was successfully grafted onto the silica surface. FTIR result of the grafted silica showed the new absorptions. The peaks at 2966,2929 and 2862 cm(-1) are assigned to CH stretching vibrations. The absorption band at 1660 cm(-1) is characteristic of C C stretching. The stretching vibration of epoxy groups that should be at 870 cm-' was missing, suggesting the epoxy groups were almost used up to react with silanol groups. A new shoulder peak appears at 3640 cm(-1), which is ascribed to - 011 stretching of C-OH which is the result of the reaction of silanol groups and ENR. TGA curves revealed ENR grafted silica showed a new step between 348 - 449 degrees C due to the decomposition of ENR, and the grafting rate reached 21.3 %. TEM images indicated the size of silica agglomerates became small obviously after modification because of the grafting layer preventing the silica particles from conglomerating. Then, compared with the silica without grafting, the properties of NR composites filled with grafted silica were investigated. The "Payne effect" results indicated that the grafted ENR molecules reduced the silica-silica interaction by enhancing the rubber-silica interaction, and so the grafted silica had better dispersibility in natural rubber ( NR) composites. Mechanical properties test of NR composites proved that the grafted silica could more effectively improve the reinforcement effect due to the strong interface combination between silica and ENR. DMA results showed that the temperature of glassy transition of ENR bound to the silica surface shifted to higher temperatures. Consequently, the composite contained the grafted silica had high strength and high hysteresis at the same time on the normal temperature. So the composites have potential application in the shocking absorber products, the tire of racing cars, and so on.

Preparation, structural characterization, and antioxidative behavior in natural rubber of antioxidant GM functionalized nanosilica

A facile and green preparation of nanosilica-supported antioxidant and its reinforcement and antioxidation effect on styrene-butadiene rubber

Preparation of halloysite nanotubes loaded antioxidant and its antioxidative behaviour in natural rubber

Preparation and Properties of High Performance Bio-based Elastomer Based on Methyl Methacrylate Grafted Natural Rubber

A Novel Rare-Earth Complex Containing Hindered Phenol and Thioether Groups for Styrene-Butadiene Rubber/silica Composites with Improved Antioxidative Properties

Functionalized graphene as an effective antioxidant in natural rubber

Effect of 3-propionylthio-1-propyltrimethoxylsilane on structure, mechanical, and dynamic mechanical properties of NR/silica composites

Preparation of Halloysite Nanotubes Supported 2-Mercaptobenzimidazole and Its Application in Natural Rubber

Effect of silane coupling agent grafted glycidyl methacrylate on hollow microsphere/natural rubber composites

Reinforcement and Antioxidation Effects of Antioxidant Functionalized Silica in Styrene–butadiene Rubber

Novel Blocked Mercaptosilane (3-Propionylthio-1-propyltrimethoxylsilane) for Natural Rubber/Silica Composite Reinforcement in Various Curing Systems

Preparation and properties of natural rubber/organic vermiculite nanocomposites

Performance Enhancement of Silica Filled Natural Rubber Nanocomposites Using Organic Deep Eutectic Solvent

PREPARATION AND CHARACTERIZATION OF THE NATURAL RUBBER COMPOSITES REINFORCED BY EPOXY NATURAL RUBBER GRAFTED SILICA WITH GOOD DISPERSIBILITY

Synthesis and Antioxidative Properties in Natural Rubber of Novel Macromolecular Hindered Phenol Antioxidants Containing Thioether and Urethane Groups

Synthesis of natural rubber-g-maleic anhydride and its use as a compatibilizer in natural rubber/short nylon fiber composites

Mechanical Properties and Thermal Resistance of Natural Rubber Nanocomposite Reinforced with Quaternized Polyvinyl Alcohol/Silica Nanoclusters

Fabrication of Multifunctional Chitosan Derivative with Long-Chain Alkene and Thiourea Structure and Its Application in Styrene-Butadiene Rubber/Silica Composites

Mesoporous silica as nanocarrier of antioxidant for highly anti-aging elastomer composites

Mechanical properties and quantum mechanical simulations of natural rubber composites with cerium complexes under aging conditions

Rheological and Dynamic Mechanical Behaviors of Short Nylon Fiber and Silica Filled Natural Rubber Compounds