Study on biocompatibility of poly(amino acid)/calcium sulfate composite as bioengineering bone
Su Bao,Jiang Dianming,Yan Yonggang,Zhao Zenghui,Li Jun
DOI: https://doi.org/10.16016/j.1000-5404.2011.01.033
2011-01-01
Abstract:Objective To evaluate the biocompatibility of poly(amino acid)/calcium sulfate(PAA/CaSO4) composite as bioengineering bone.Methods The PAA in the composite consists of 6-aminohexanoic acid,glycine,alanine,phenylalanine,proline,lysine,and hydroxyproline.Physiological saline lixivium of the composite was used in acute toxicity test,hemolysis test,micronucleus test,intradermal irritation test,pyrogen test,and cytotoxicity test to evaluate the biocompatibility of the material.Results The activity of mice was normal in the acute toxicity test.No animal died and no toxicity symptom or adverse effect was shown within 7 d.The average daily weight increases showed no statistically significant difference(P>0.05) between the experimental and control groups after 7 d.The hemolysis rate of the lixivium was 2.01%,which was lower than the national standard(<5%).The micronucleus rates showed no statistically significant difference(P>0.05) between three experimental groups and the negative control group(each group's micronucleus rate was between 0.4 and 0.6),and potential mutagenicity was not observed in the micronucleus test.The maximum increase of body temperature in the experimental group was 0.4 ℃,and the total body temperature increase of the three experimental animals was 1.1 ℃,which met the national standard(<1.4 ℃).Intradermal irritation test results showed no obvious erythema,edema,or skin necrosis in the experimental and negative control groups,with a primary irritation index of 0.01-0.02,indicating very slight irritation.In the cytotoxicity test,the relative growth rates of two experimental groups and the negative control group were all above 90%,and the toxicity of PAA/CaSO4 composite lixivium was graded 0 or 1,indicating no cytotoxicity.Conclusion PAA/CaSO4 composite has good biocompatibility.