Abstract:The tension-compression yield asymmetry caused by the strengthening of Mg-Zn-Gd-Zr alloy due to extrusion deformation is an important issue that must be addressed in its application. In this study, the effects of loading direction on the tensile and compressive mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy were systematically investigated. As the loading angle (the angle between the loading direction and the extrusion direction) increases from 0° to 30°, 45°, 60° and 90°, the tensile yield strength decreases more significantly than the compressive yield strength. Consequently, the tension-compression yield asymmetry is gradually improved. Additionally, the ultimate compressive strength decreases more markedly than the ultimate tensile strength with the increment of the loading angle. In tensile tests conducted at 0°, 30° and 45°, two distinct stages of decreasing strain hardening rates are typically observed. For the 60° and 90° tensile tests, one unusual ascending stage of strain hardening rate is observed. For all compressive tests, three stages of strain hardening are consistently noted; however, the increment in strain hardening rate caused by {10–12} extension twinning decreases with the increasing loading angle. A model combining loading angle and Schmid factor distribution was established. The calculated results indicate that the dominant deformation modes during the yielding process also vary significantly with the loading conditions. This clarification highlights the differences in yield strength variations between tension and compression. Finally, an analysis of the plane trace and crack propagation direction near the fracture surface reveals the fracture mechanisms associated with tensile and compressive tests at different loading directions. This study promotes understanding of the mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy under different loading directions, and helps to thoroughly elucidate the anisotropic effects of texture on the mechanical properties of magnesium alloys.

Unloading Yield Effect in a Twin-Roll-cast Mg–3Al–1Zn Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Stress relaxations during cyclic loading-unloading in precipitation hardened Mg-4.5Zn

Effect of Loading Direction on Tensile-Compressive Mechanical Behaviors of Mg-5Zn-2Gd-0.2Zr Alloy with Heterogeneous Grains

Microstructures, hot tensile deformation behavior and constitutive modeling in a superlight Mg-2.76Li-3Al-2.6Zn-0.39Y alloy

Unloading behaviors of the rare-earth magnesium alloy ZE10 sheet

Room-Temperature Strengthening, Portevin-Le Chatelier Effect, High-Temperature Tensile Deformation Behavior, and Constitutive Modeling in a Lightweight Mg-Gd-Al-Zn Alloy

Hot deformation behavior of novel high-strength Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy

The abnormal flow behavior of Mg-9Gd-4Y-2Zn-0.5Zr alloy during hot tensile deformation at high temperature and low strain rate

Microstructure and Yield Plateau of an Annealed Extruded Mg-Y-Cu Alloy

Effects of trace Zn on the deformation mechanisms of Mg‐Gd‐Y‐Zr alloy investigated by in‐situ synchrotron diffraction

The Effect of Unloading Positions and Times on Sheet Metal’s Stress-Strain Curve

In Situ Monitoring of Dislocation, Twinning, and Detwinning Modes in an Extruded Magnesium Alloy under Cyclic Loading Conditions

Effects of extrusion ratio and subsequent heat treatment on the tension-compression yield asymmetry of Mg-4.58Zn-2.6Gd-0.18Zr alloys

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Microstructure and yield phenomenon of an extruded Mg-Y-Cu alloy with LPSO phase

Hot Deformation Behavior and Microstructure Evolution of a Novel High-Zn Containing Al-Zn-Mg-Cu-Zr Alloy

Mechanical properties and fracture behavior of Mg–3Al–1Zn alloy under high strain rate loading

Fatigue deformation mechanism of the Mg–Nd alloys

High Strain Rate Quasi-Superplasticity Behavior in an Ultralight Mg-9.55Li-2.92Al-0.027Y-0.026Mn Alloy Fabricated by Multidirectional Forging and Asymmetrical Rolling

Hot compression behavior and microstructure evolution of Mg-Gd-Y-Zn-Zr alloy