Prediction of Ir 0.5 M 0.5 O 2 (M = Cr, Ru or Pb) Mixed Oxides as Active Catalysts for Oxygen Evolution Reaction from First-Principles Calculations

Ya Song,Ji Yang,Xue-Qing Gong

DOI: https://doi.org/10.1007/s11244-015-0404-y

IF: 2.781

2015-01-01

Topics in Catalysis

Abstract:Hydrogen generation via water splitting suffers from a substantial energy loss mainly due to the sluggish oxygen evolution reaction (OER) at anode. The noble metal oxide, such as iridium dioxide (IrO 2 ), is considered as a promising oxygen-evolving catalyst in proton exchange membrane based electrolysis cell, though it still needs to be improved due to the large over-potential. At the same time, composite materials containing lower amount of Ir without appreciable loss in electrocatalytic activity are also in high demand. By using the first-principles density functional theory calculations, we have studied the OER at IrO 2 substituted with M (Ti, Cr, Mn, Ru, Rh, Pt, Sn, Pb) to search for the candidate catalysts with lower over-potential. Our calculation results show that the formation of Ir 0.5 Ti 0.5 O 2 solid solution is thermodynamically the easiest and Pt cation is the most difficult to be substituted into IrO 2 lattice. When OER occurs, the surfaces for pure and doped IrO 2 are readily covered with O. The formation of adsorbed HOO at Ir 0.5 M 0.5 O 2 catalysts is the potential-determining step which gives the theoretical over-potential close to that of pure IrO 2 . The free energy changes of this step increase in doped IrO 2 systems with Ti, Mn, Rh, Pt or Sn, while they reduce at Ir 0.5 Cr 0.5 O 2 , Ir 0.5 Ru 0.5 O 2 and Ir 0.5 Pb 0.5 O 2 catalysts. In particular, compared to the pure IrO 2 , the binding strength of O is weakened more significantly than that of HOO at the Cr-, Ru- and Pb-doped IrO 2 , leading to the reduction of the free energy differences.