Improving anti-fouling properties of alumina tubular microfiltration membranes through the use of hydrophilic silica nanoparticles for oil/water separation
Anirban Ghosh,Ghader Mahmodi,Michael Miranda,Songpei Xie,Madelyn Shaw,Mark Krzmarzick,David J. Lampert,Seok-Jhin Kim,Clint P. Aichele,Anirban GhoshGhader MahmodiMichael MirandaSongpei XieMadelyn ShawMark KrzmarzickDavid J. LampertSeok-Jhin KimClint P. Aichelea School of Chemical Engineering,Oklahoma State University,Stillwater,OK,USAb School of Civil and Environmental Engineering,Oklahoma State University,Stillwater,OK,USAc Department of Civil,Architectural,and Environmental Engineering,Illinois Institute of Technology,Chicago,IL,USA
DOI: https://doi.org/10.1080/01496395.2023.2259605
IF: 2.799
2023-10-01
Separation Science and Technology
Abstract:In this study, hydrophilic silica nanoparticles (Si NPs) were used to modify ╬▒-alumina tubular membranes to improve their performance in terms of flux, oil rejection, and anti-fouling properties. Our work focuses on enhancing membrane performance, particularly for difficult applications such as produced water treatment. The prepared membranes were applied for oil-in-water emulsion treatment. After coating hydrophilic Si NPs, the oil contact angle improved from 133.8┬░ to 171.4┬░. To prevent Si NPs from leaching off the surface of ╬▒-alumina tubular membranes, polyvinyl alcohol was used to coat the membranes as a pre-treatment step before Si NP modification. After coating the membrane with Si NPs, the roughness of the membrane surface decreased, likely leading to less fouling. After coating Si NPs, Total Organic Carbon rejection increased from 93.1% for pristine ╬▒-alumina tubular membranes to 97.7% for silica-modified membranes because of hydrophilic improvements of the modified membranes. The Si NP coating improved the anti-fouling property of membranes with the flux recovery ratio increasing from 71.3% for pristine ╬▒-alumina tubular membranes to 85.9% for silica-modified membranes. Scanning Electron Microscopy, Energy-dispersive X-ray spectroscopy, oil contact angle, and Atomic Force Microscopy characterization tests were done. The tests showed successful Si NPs impregnation and altered wettability.
engineering, chemical,chemistry, multidisciplinary