Modeling of Damage Driven Fracture Failure of Fiber Post-Restored Teeth.

Binting Xu,Yining Wang,Qing Li
DOI: https://doi.org/10.1016/j.jmbbm.2015.05.006
2015-01-01
Abstract:Mechanical failure of biomaterials, which can be initiated by either violent force, or progressive stress fatigue, is a serious issue. Great efforts have been made to improve the mechanical performances of dental restorations. Virtual simulation is a promising approach for biomechanical investigations, which presents significant advantages in improving efficiency than traditional in vivo/in vitro studies. Over the past few decades, a number of virtual studies have been conducted to investigate the biomechanical issues concerning dental biomaterials, but only with limited incorporation of brittle failure phenomena. Motivated by the contradictory findings between several finite element analyses and common clinical observations on the fracture resistance of post-restored teeth, this study aimed to provide an approach using numerical simulations for investigating the fracture failure process through a non-linear fracture mechanics model. The ability of this approach to predict fracture initiation and propagation in a complex biomechanical status based on the intrinsic material properties was investigated. Results of the virtual simulations matched the findings of experimental tests, in terms of the ultimate fracture failure strengths and predictive areas under risk of clinical failure. This study revealed that the failure of dental post-restored restorations is a typical damage-driven continuum-to-discrete process. This approach is anticipated to have ramifications not only for modeling fracture events, but also for the design and optimization of the mechanical properties of biomaterials for specific clinically determined requirements.
What problem does this paper attempt to address?