Abstract:Melt-branching of high density polyethylene (HDPE), through free radical reaction, was carried out in the presence of dicumyl peroxide (DCP) as the initiator, neopentyl glycol diacrylate (NPGDA) as difunctional monomer, and zinc dimethyldithiocarbamate (ZDMC) as the free radical concentration regulator. Results showed that HDPE with long branching chains and low gel content was obtained under optimized reaction time, which was corresponding to the reaction peak-the second peak in the torque curve. After this melt branching reaction, the molecular weight of the modified HDPE increased slightly and its molecular weight distribution became wider compared with the virgin linear HDPE. The branching degree of modified HDPE increased with increased monomer content, with a more apparent shear thinning in the complex viscosity versus frequency (eta*-omega) plots. The regularity of the polyethylene molecule was broken up after the long branching chains being introduced, which decreased the degree of crystallinity in the modified polyethylene. While the crystallization onset temperature improved and the size of spherocrystal obviously decreased with the nucleation of the long branching chains in the modified HDPE, a threshold value for the branching was shown to exist by the environmental stress cracking resistance test on the modified polyethylene. When monomer content exceeded 0.6 phr, the molecule shape of the long chain branched polyethylene transformed from asymmetric star-like to comb-like, which made the environmental stress cracking resistance time be larger than 1000 h, the strength, the modulus and the impact toughness were all enhanced at the same time. However, the branching degree was reduced with an overlong time mixing and melt-branching reaction, the comb-like branching chains were not formed by consequence, which made an inapparent enhancement for the environmental stress cracking resistance performance of the modified polyethylene.

Selectivity of Shear Flow on Chains for the Degradation Reaction of Melt Polyolefin Elastomer with Dicumyl Peroxide

Oxidative Upcycling of Polyolefin Wastes into the Dynamically Cross-Linked Elastomer

Preparation Of Comb-Shaped Polyolefin Elastomers Having Ethylene/1-Octene Copolymer Backbone And Long Chain Polyethylene Branches Via A Tandem Metallocene Catalyst System

Synthesis and Characterization of Polyolefin Thermoplastic Elastomers: A Review

Study on Crosslinking of Polyethylene–Octene Elastomer with Dicumyl Peroxide

Thermo‐oxidative degradation of ultrahigh molecular weight poly(ethylene oxide) in volatile organic solvents

Rheological Insights into the Degradation Behavior of PP/HDPE Blends

Shear relaxation behavior for degraded polypropylene melt in torque rheometer

Degradable Thermoresponsive Polyesters by Atom Transfer Radical Polyaddition and Click Chemistry

Preparative temperature rising elution fractionation of polyolefin elastomer and its chain microstructure

In vitro enzymatic degradation of the PTMC/cross-linked PEGDA blends

Correlation of Enzymatic Depolymerization Rates with the Structure of Polyethylene-Like Long-Chain Aliphatic Polyesters

Chain conformation and dynamics in ultrahigh molecular weight polyethylene melts undergoing extensional–shear coupled flow: insight from dissipative particle dynamics simulation

Crystallization, structure, and enhanced mechanical property of ethylene‐octene elastomer crosslinked with dicumyl peroxide

A DFT mechanistic study on the N‐acyloxyamine‐initiated controlled degradation of polypropylene

Effect of Structure and Morphology on Photo-Oxidation Degradation of Polyethylene

Thermal characteristics and temperature profile changes of structurally different polyethylenes with peroxide modifications

The rheology of ultra-high molecular weight poly(ethylene oxide) dispersed in a low molecular weight carrier

The Effect of Dialkyl Peroxide Crosslinking on the Properties of LLDPE and UHMWPE

Bulk Erosion Degradation Mechanism for Poly(1,8-octanediol- co-citrate) Elastomer: An In Vivo and In Vitro Investigation

Melt Branching of High Density Polyethylene and Influences on Its Performances