Abstract:For advanced performance lithium-ion batteries (LIBs) various novel electrode materials with high energy density have been extensively investigated. Cobaltosic oxide (Co3O4), commonly used as an anode in LIBs, has attracted much interest because of its high theoretical specific capacity (890 mAh center dot g(-1)), high tap density, and stable chemical properties. However, its practical use has been hindered because of its low electronic conductivity and poor rate capability. To address these problems, we investigated a liquid phase precipitation method followed by thermal treatment and obtained a unique lamellar Co3O4 powder. Its X-ray diffraction (XRD) diffraction peaks match the standard pattern for cubic phaseCo(3)O(4) with good crystallinity. We found that the Co3O4 powder consists of many irregular sheets (1.5-3.0 mu m in diameter, 100-300 nm in thickness) with numerous poles by scanning electronmicroscopy (SEM). Additionally, the surface area was about 30.5m(2) center dot g-1, and this was calculated from BET nitrogen adsorption isotherm measurement data. Remarkably, perfect performance was obtained as evaluated by electrochemical measurements, including a high initial discharge capacity (1444.5 mAh center dot g(-1) at 0.1C) and excellent capacity retention (charge capacity after 50 cycles was still greater than 1100.0 mAh center dot g(-1) at 0.1C). However, its rate capability was still not adequate (75.3% of the first charge capacity after 50 cycles at 1C). To improve the rate capability, commercial carbon nanotubes (CNTs) mixed with the Co3O4 powder was used to enhance the electronic conductivity. The charge capacity retention ratios were 96.3% after 70 cycles at 1C and 97.0% after 50 cycles at 2C. Therefore, enhanced electrochemical performance with impressive rate capability was obtained, as expected.

Constructing CoFe2O4 with cubic structure by Prussian blue to provide high-performance anodes for lithium-ion batteries

NiO/NiFe2O4 nanocubes derived from Prussian blue as anode materials for Li-ion batteries

Highly Crystalline Prussian Blue Cubes Filled with Tin Oxide As Anode Materials for Lithium-Ion Batteries

In Situ Construction of Heterostructured Co3O4/CoP Nanoflake Arrays on Carbon Cloth as Binder-Free Anode for High-Performance Lithium-Ion Batteries

Highly efficient Co3O4/CeO2 heterostructure as anode for lithium-ion batteries

Prussian blue analogues-derived nitrogen-doped carbon-coated FeO/CoO hollow nanocages as a high-performance anode material for Li storage

Prussian blue microcubes-derived FeF 3 cathodes for high-energy and ultra-stable lithium and lithium-ion batteries

Synthesis of Porous CoFe2O4 Octahedral Structures and Studies on Electrochemical Li Storage Behavior

Micro-/Nanostructured Co3O4 Anode with Enhanced Rate Capability for Lithium-Ion Batteries

Constructing 3D Sandwich-Like Carbon Coated Fe2O3/helical Carbon Nanofibers Composite As a Superior Lithium-Ion Batteries Anode

Synthesis and Modification of a Lamellar Co3O4 Anode for Lithium-Ion Batteries

Fe3O4@C-500 anode derived by commercial ammonium ferric citrate for advanced lithium ion batteries

Porous Polyhedral and Fusiform Co3O4 Anode Materials for High-Performance Lithium-Ion Batteries

Co3O4/LaCoO3 nanocomposites derived from MOFs as anodes for high-performance lithium-ion batteries

Facile synthesis and high lithium storage properties of mesoporous polypyrrole coated CoFe2O4 nanofibers

MOF-derived iron sulfide nanocomposite with sulfur-doped carbon shell as a promising anode material for high-performance lithium-ion batteries

A general strategy for enabling Fe3O4 with enhanced lithium storage performance: Synergy between yolk-shell nanostructures and doping-free carbon

MOF-derived CoFe2O4/FeO/Fe nanocomposites as anode materials for high-performance lithium-ion batteries

Facile synthesis of FeCO3/nitrogen-doped carbon dot composites for lithium-ion battery anodes

Co-Precipitation Synthesis of Co3[Fe(CN)6]2·10H2O@rGO Anode Electrode for Lithium-Ion Batteries

In-situ rooting biconical-nanorods-like Co-doped FeP @carbon architectures toward enhanced lithium storage performance