Facile preparation and properties of high nitrogen-containing Fe/Co/N co-doped three-dimensional graphene bifunctional oxygen catalysts for zinc air battery

Changhui Ji,Tingwei Zhang,Peng Sun,Ping Li,Jigang Wang,Lei Zhang,Yinggang Sun,Wenjie Duan,Zhongfang Li

DOI: https://doi.org/10.1016/j.ijhydene.2023.03.333

IF: 7.2

2023-04-10

International Journal of Hydrogen Energy

Abstract:Fe/Co/N co-doped multi-channel interpenetrating three-dimensional graphene catalyst (FeCo–N-3D-HG) with good oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) catalytic performances is prepared by a facile method, using poly (2,5-benzimidazole) (ABPBI), iron salt, cobalt salt and nanometer CaCO 3 (template). ABPBI forms a complex with iron and cobalt ions and the complex is coated on the surface of CaCO 3 . The pyrolysis process is carried out in an Ar gas protection, the template is removed by acid to obtain FeCo–N-3D-HG. The results show that FeCo–N-3D-HG is three-dimensional multi-layered graphene structure with multi-channels. The catalytic performance of ORR (E 1/2 = 0.860 V vs RHE) is better than 20 wt% Pt/C in O 2 saturated 0.1 M KOH electrolyte. The catalyst also shows similar OER performance with the RuO 2 in 1 M KOH solution. The prepared zinc-air battery exhibits outstanding peak power density (261.7 mW cm −2 ), preeminent specific capacity (760.1 mAh g −1 ), and good cycle durability (150 h).

energy & fuels,electrochemistry,chemistry, physical