Functionalization of cotton fabrics through PEI/PA/FeAl ternary system with enhanced flame retardance and antibacterial properties
Qingyi Li,Yakun Zong,Yuanzhang Jiang,Jun Zhang,Ruifang Zhao,Jianming Chen,Yidong Shi,Lin Tan
DOI: https://doi.org/10.1007/s10570-024-05979-6
IF: 6.123
2024-05-31
Cellulose
Abstract:Cotton fabrics are widely used in clothing, packaging, and medical applications because of their excellent comfort, breathability, and low cost. However, it poses a threat to use them in specific scenarios, where flame retardance and antibacterial activity are highly desired. In this work, we propose the functionalization route by using layer-by-layer assembly of polyethyleneimine (PEI), phytic acid (PA), iron (Fe 3+ ), and aluminum (Al 3+ ) ions on cotton fabrics. Interestingly, the modified cotton fabric showed good biocompatibility in the cell viability (> 70%) and hemolysis ( 99% due to the presence of Fe 3+ and Al 3+ that work in a synergistic manner. In term of flame retardance, the modified cotton fabric exhibited self-extinguishing characteristics in vertical burning experiments, with the Limiting Oxygen Index (LOI) of 35.0%. The excellent flame-retardant property was further supported by the results in cone calorimetry test, thermal gravimetric analysis, and TG-IR test, elucidating the underlying mechanism that rapid formation of dense char layer by the thermal decomposition of PEI/PA/FeAl system is effective to prevent the spreading of flame and thus protect the cotton from burning. This work provides a strategy to achieve multifunctionality on cotton fabrics, which may inspire the design on other types of fabrics or materials for extended applications.
materials science, textiles,polymer science, paper & wood