Non-flammable alginate nanocomposite aerogels prepared by a simple freeze drying and post-crosslinking method.

Ke Shang,Wang Liao,Juan Wang,Yu-Tao Wang,Yu-Zhong Wang,David A Schiraldi

DOI: https://doi.org/10.1021/acsami.5b09768

IF: 9.5

2016-01-01

ACS Applied Materials & Interfaces

Abstract:Non-flammabile materials based on renewable ammonium alginate and nano fillers (nano-scale magnesium hydroxide, nano-scale aluminum hydroxide, layered double hydroxide, sodium montmorillonite and Kaolin) were fabricated through a simple, environmentally-friendly freeze drying process using water as the solvent. A simple and economic post-crosslinking method was used to obtain homogeneous samples. The microstructure of the crosslinked alginate aerogel shows a three dimension network. These materials exhibit low densities (0.064-0.116 g cm-3), low thermal conductivities (0.024-0.046 W/m K) and useful mechanical strengths (0.7-3.5 MPa). The aerogels also exhibit high thermal stabilities and achieve inherent non-flammability with Limiting Oxygen Indexes (LOI) higher than 60. Related properties were conducted and analyzed by cone calorimeter (CC), thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and X-Ray photoelectron spectroscopy (XPS). These results combine to suggest promising prospects for use of these aerogel nanocomposites in a range of applications.