Structure-property relationship of poly(2,6-dimethyl-1,4-phenylene oxide) anion exchange membranes with pendant sterically crowded quaternary ammoniums
Zhiru Liu,Li Bai,Shasha Miao,Chao Li,Ji Pan,Yu Jin,Dongrui Chu,Xiaomeng Chu,Lei Liu
DOI: https://doi.org/10.1016/j.memsci.2021.119693
IF: 9.5
2021-11-01
Journal of Membrane Science
Abstract:Steric hindrance engineering is of great significance to the preparation of new stable organic cations and durable polymeric anion exchange membrane materials. In this work, we presented a study of the structure-property relationship in quaternized poly (2,6-dimethyl-1,4-phenylene oxide) containing bulky n-propyl, isopropyl, or cyclohexyl-functionalized quaternary ammonium moieties. To our surprise, PPO-iP membranes possessing isopropyl-based QA cations showed higher water uptake than n-propyl- and cyclohexyl-containing analogues (PPO-nP and PPO-CH), in which obvious microphase-separated morphology was found. Thus, PPO-iP membranes displayed the highest hydroxide conductivity at 20 °C in water (37.3 mS/cm, IEC = 1.90 mmol/g). A standard protocol (1 M or 2 M NaOH at 60 °C) was used to determine the chemical stability of model cations and membranes both having sterically crowded QAs. Minor loss (<2%) in conductivity was observed for PPO-CH membranes after the treatment in 2 M NaOH at 60 °C for 216 h, highlighting the excellent alkaline stability, while significant degradation of PPO-iP and PPO-nP was confirmed by NMR characterization of the aged samples. In addition, the prepared PPO-based AEMs having sterically crowded QA cations were compared in alkaline H2/O2 fuel cells, demonstrating that the highly conductive PPO-iP membrane exhibited a peak power density of 182 mW/cm2 under optimized testing conditions.
engineering, chemical,polymer science